Abstract:Although inorganic all-solid-state Li-ion batteries (ASSLiBs) using stable oxide solid electrolytes are considered to be promising candidates for future energy storage devices, their relatively high cell impedance due to the restricted contact area and interfacial stability results in unsatisfactory electrochemical performance and fast capacity fading. The mechanism limiting performance and cycle life in such ASSLiBs still lack study and hence understanding. To overcome this bottleneck, we prepared a bulk ASSLiB, where a MnO2–CNT nanocomposite is used as a high-voltage anode to prevent reduction of the electrolyte by a lithium anode, high-voltage LiNi0.5Mn1.5O4 is used as a cathode, and ambient-air stable Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is chosen as a solid-state electrolyte (SSE). This ASSLiB shows a maximum discharge capacity of 82 mAh g–1 at 0.15C and 23.8 °C. The electrochemical impedance study of the cell reveals a decrease in impedance after solid interface layer formation in cycle 1 followed by an increase after electrode lithiation/delithiation. Electrochemical evaluation and first-principles calculations were used to explore the decomposition of the LAGP after charge/discharge cycles. Decomposition of LAGP with the assistance of Li ions and free electrons from voids and grain boundaries leads mainly to the formation of Li4P2O7, Li3PO4, Ge5P6O25, AlPO4, and GeO. Finite element method simulations reveal that the volume expansion due to the formation of the decomposition products Li4P2O7, Li3PO4, and AlPO4 results in a maximum internal stress of 2.5–125 GPa for various Li excess ratios ranging from 0 to 6. This by far exceeds the failure stress of LAGP and results in crack formation and growth in the SSE on multiple cycling.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01564.Characteristics of the MnO2–CNT nanocomposite; Nyquist plots; CV curve; TOF-SIMS preparation and characterization; SEM images; formation energy analysis of the LAGP decomposition products; FEM model and parameters; and cycle performance comparison (PDF)This article has not yet been cited by other publications.

Failure Mechanism and Interface Engineering for NASICON Structure All-solid-state Lithium Metal Batteries.

Electromechanical Failure of NASICON-Type Solid-State Electrolyte-Based All-Solid-State Li-Ion Batteries

Chemomechanical Failure Mechanism Study in NASICON-Type Li1.3Al0.3Ti1.7(PO4)3 Solid-State Lithium Batteries

Safe LAGP-based all solid-state Li metal batteries with plastic super-conductive interlayer enabled by in-situ solidification

Bifunctional in Situ Polymerized Interface for Stable LAGP‐Based Lithium Metal Batteries

Antiperovskite Ionic Conductor Layer for Stabilizing the Interface of NASICON Solid Electrolyte Against Li Metal in All‐Solid‐State Batteries**

Interface Engineering of a NASICON-Type Electrolyte Using Ultrathin CuS Film for Lithium Metal Batteries

Stable Li|LAGP Interface Enabled by Confining Solvate Ionic Liquid in a Hyperbranched Polyanionic Copolymer for NASICON-Based Solid-State Batteries

Integrated Interface Configuration by In-Situ Interface Chemistry Enabling Uniform Lithium Deposition in All-Solid-state Lithium Metal Batteries

Design of a Multifunctional Interlayer for NASCION‐Based Solid‐State Li Metal Batteries

Boosting fast interfacial Li+ transport in solid-state Li metal batteries via ultrathin Al buffer layer

Stabilization of NASICON-Type Electrolyte against Li Anode via an Ionic Conductive MOF-Incorporated Adhesive Interlayer

Codependent failure mechanisms between cathode and anode in solid state lithium metal batteries: mediated by uneven ion flux

The construction of multifunctional solid electrolyte interlayers for stabilizing Li6PS5Cl-based all-solid-state lithium metal batteries

Stabilized Cathode/Sulfide Electrolyte Interface through Conformally Interfacial Nanocoating for All-Solid-State Batteries

Smart construction of multifunctional Li1.5Al0.5Ge1.5(PO4)3|Li intermediate interfaces for solid-state batteries

Stabilizing the Interface of NASICON Solid Electrolyte Against Li Metal with Atomic Layer Deposition.

Manipulating Interfacial Nanostructure to Achieve High‐Performance All‐Solid‐State Lithium‐Ion Batteries

Enabling High-Performance NASICON-Based Solid-State Lithium Metal Batteries Towards Practical Conditions

Self-Healing Janus Interfaces for High-Performance LAGP-Based Lithium Metal Batteries

Stabilizing Interface Between Li10SnP2S12 and Li Metal by Molecular Layer Deposition