Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Mechanical Properties and Microstructure Evolution of Pressureless-Sintered B4C–SiC Ceramic Composite with CeO2 Additive

High-performance B4C matrix composites fabricated from the B4C–Si–CeO2 system via reactive hot pressing

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites

Mechanical properties and pre-oxidation behavior of spark plasma sintered B4C ceramics using (Ti3SiC2+CeO2/La2O3) as sintering aid

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Microstructure and properties of hot pressed TiB2 and SiC reinforced B4C–based composites

Influence of Silicon Addition on the Sintering Behavior and Mechanical Properties of Boron Carbide by SPS Process

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

Effect of CeO2 Content on Microstructure and Properties of SiCp/Al-Si Composites Prepared by Powder Metallurgy

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Pressureless sintering and ablation behavior of PyC-Csf/ZrB2-SiC-ZrC ceramics doped with B4C

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites

The Effects of Transition Metal Oxides (Me = Ti, Zr, Nb, and Ta) on the Mechanical Properties and Interfaces of B4C Ceramics Fabricated via Pressureless Sintering

Effect of the Addition of Carbon on the Sintering Properties of Boron Carbide Ceramics Prepared by Pressureless Sintering

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

B4C-SiC composites with tuneable mechanical properties: Role of Al2O3 - Y2O3 sintering additives

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Pressureless sintering of boron carbide ceramics with Al–Si additives

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

The effect of transition metal carbides MeC (Me = Ti, Zr, Nb, Ta, and W) on mechanical properties of B4C ceramics fabricated via pressureless sintering