Abstract:The picture shows vermiculite modified with silane coupling agent KH570. VMT/PBAT and OVMT/PBAT composite films were prepared by solution method. The structure, thermal properties, crystalline properties, rheological properties, cross‐sectional microstructure, and tensile properties of the pure PBAT films, VMT/PBAT, and OVMT/PBAT composite films were tested and comparatively analyzed. The results showed that the OVMT was uniformly dispersed in the matrix in the composites with the addition of modifiers, the thermal stability of the composite films was relatively improved, the initial decomposition temperature of the OVMT/PBAT composite films was about 2–4°C higher than that of the VMT/PBAT composite films, and the complex viscosity was also greater with improved viscoelasticity. The mechanical properties of the OVMT/PBAT‐20% composite films were higher than those of the VMT/PBAT composite films. The mechanical properties of the OVMT/PBAT‐20% films were 35.9% higher in tensile strength and 10.8% higher in elongation at break than the VMT/PBAT‐20% films. Vermiculite (VMT) was used as a filler and it was modified with silane coupling agent KH570 to produce OVMT. VMT/PBAT and OVMT/PBAT composite films were prepared using the solution method using polybutylene terephthalate (PBAT) as a matrix. The structure, thermal properties, crystalline properties, rheological properties, cross‐sectional microstructure, and tensile properties and antibacterial properties of the pure PBAT film, VMT/PBAT, and OVMT/PBAT composite films were tested, including comparative analysis. The results showed that VMT was successfully modified with silane coupling agent to produce OVMT. Furthermore, the thermal stability of VMT/PBAT and OVMT/PBAT composite films decreased compared with pure PBAT film. As the content of VMT and OVMT increases, the energy storage modulus and loss modulus of VMT/PBAT and OVMT/PBAT composite films increase, while the loss factor, complex viscosity and crystallinity gradually decrease. Additionally, the tensile strength and elongation at break of VMT/PBAT and OVMT/PBAT composite films decrease. All three films had no effect on Staphylococcus aureus or Escherichia coli. The modification of VMT with the silane coupling agent KH570 improved the compatibility of OVMT with PBAT, resulting in improved mechanical properties of the OVMT/PBAT composite film compared with the VMT/PBAT composite film. The mechanical properties of the OVMT/PBAT‐20% composite film increased by 35.9% in tensile strength and 10.8% in elongation at break compared with the VMT/PBAT‐20% composite film. Highlights VMT successfully modified with silane coupling agent to produce OVMT. The modification promotes the compatibility of the filler with PBAT. VMT modification helps to improve the mechanical properties of composite materials. Vermiculite modification helps to improve the toughness of composite materials.

Preparation of POSS-triol/wollastonite Composite Particles by Liquid Phase Mechanochemical Method and Its Application in UV Curable Coatings

The Preparation and Characterization of PMMA/POSS-OH Hybrid Fiber

Mechanical Grinding Preparation and Characterization of TiO2-Coated Wollastonite Composite Pigments

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

Synthesis of Trivinylisooctyl POSS and Its Application in UV-Curing of Polyurethane Acrylate Coatings

Preparation of Transparent, Hard Thermochromic Polysiloxane/tungsten-Doped Vanadium Dioxide Nanocomposite Coatings at Ambient Temperature

Polyhedral Oligomeric Silsesquioxane (POSS) As Reinforcing Agent for Waterborne Polyurethane Coatings on Wood

The Preparation and Characterization of Aqueous Nanosilica/Polyester Composite Resin and Coatings

Environmentally Friendly Wollastonite@tio2 Composite Particles Prepared by a Mechano-Chemical Method

"Thiol-Ene" Photo-Cured Hybrid Materials Based on Poss and Renewable Vegetable Oil

Preparation and characterization of ultraviolet-curable nanocomposite coatings initiated by benzophenone/n-methyl diethanolamine

Preparation of polyacrylate/nano-SiO2composite emulsion by Pickering emulsion polymerization and its potential application in coating materials

Preparation of functional ZnO nanoparticles and their application as UV photosensitizer and reinforcing agent for waterborne polyurethane acrylate composite coating

Nanostructures and surface dewettability of epoxy thermosets containing hepta(3,3,3-trifluoropropyl) polyhedral oligomeric silsesquioxane-capped poly(ethylene oxide).

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Photocured Zwitterionic Coatings Containing POSS for Antifogging Applications

Preparation and characterization of Al 2O 3-POSS hybrid films on quartz fiber

Surface functionalization of MoS2 with POSS for enhancing thermal, flame-retardant and mechanical properties in PVA composites

Preparation of silica-coated poly(styrene-co-4-vinylpyridine) particles and hollow particles.

Preparation and properties of silane coupling agent modified vermiculite and its composite films

Preparation of VOx/SiO2-dope Copolymer Super-Slippery Surface Composites