Abstract:The spinel lithium-ion battery anode material Li 4 Ti 5 O 12 (LTO) exhibits stable cycling and is less prone to lithium dendrite and solid electrolyte interphase (SEI) films. However, its theoretical capacity and conductivity are low within the electrochemical window of 1.0–3.0 V. In this study, we utilized active carbon (AC) coated and micron Silicon (Si) doped Li 4 Ti 5 O 12 , applying an extended electrochemical window of 0.01–3.0 V during cycling to enhance the material's electrochemical performance. Our investigation revealed that bare LTO sample as well as those with single Silicon doping or active carbon coating experienced rapid decay during high-rate long cycling tests. Conversely, the Silicon-carbon composite LSiAC sample (87 wt% Li 4 Ti 5 O 12 + 3 wt% AC + 10 wt% Si) demonstrated a capacity of 349.19 mAh g −1 (98.28%) at a 1C rate after 200 cycles, and achieved a capacity of 196.56 mAh g −1 (89.37%) after 1000 cycles at a 5C rate,; in comparison, bare LTO exhibited capacities of only 230 .98 mAh g −1 (1C-89.71%)and 145.63 mAh g −1 (5C-82.48%). This improvement can be attributed to three factors: first, the active carbon enhances material conductivity while the active carbon coating and SEI films simultaneously as a barrier isolating Li 4 Ti 5 O 12 from the electrolyte LiPF 6 , thereby preventing structural degradation; second, micron Si doping into Li 4 Ti 5 O 12 crystals introduces additional capacity and leads to an appropriate amount of expansion during cycling, effectively increasing crystal plane spacing and facilitating Li + migration. Final, the multi-layer core–shell structure consisting of Li 4 Ti 5 O 12 , active carbon coating, and SEI films acts as the buffer successfully limits the Si-Li 15 Si 4 phase transition volume expansion. The proposed modification process is straightforward and environmentally friendly, making it suitable for industrial-scale production. This approach holds promise in bolstering the competitiveness of spinel Li 4 Ti 5 O 12 as an anode material in the Lithium-ion battery market. Graphical

Unveiling the Synergic Roles of Mg/Zr Co-Doping on Rate Capability and Cycling Stability of Li4Ti5O12

Elucidation of Synergistic Effect of Mg-co-doping on Electrochemical Performance of Mn-doped LiNiO2

Tuning the Crystal and Electronic Structure of Li4Ti5O12 Via Mg/La Co-doping for Fast and Stable Lithium Storage

Structural Analysis and Electrochemical Studies of Carbon Coated Li4ti5o12 Particles Used As Anode for Lithium Ion Battery

Zr-doped Li4Ti5O12 Anode Materials with High Specific Capacity for Lithium-Ion Batteries

Tuning fermi level and band gap in Li 4 Ti 5 O 12 by doping and vacancy for ultrafast Li + insertion/extraction

Feasibility to Improve the Stability of Lithium-Rich Layered Oxides by Surface Doping

Synergetic effect of Ti-Mg-Sb tri-doping on enhanced electrochemical performance of LiCoO 2 at 4.6 V

Advanced electrochemical performance of Li4Ti5O12-based materials for lithium-ion battery: Synergistic effect of doping and compositing

Zn/Ti dual concentration-gradients surface doping to improve the stability and kinetics for Li-rich layered oxides cathode

Unraveling the Distinct Roles of Mg Occupation on Li or Co Sites on High-Voltage LiCoO 2

Stable Cycling of LiCoO2 at 4.55 V Enabled by Combined Mg Doping and Surface Coating of NASICON-type Electrolyte

Freeze-drying synthesis of metal element (Zr, Cr, Co)–doped Li4Ti5O12 anode material for enhanced electrochemical energy storage in lithium-ion batteries

Effect of Si Doping and Active Carbon Surface Modifications on the Structure and Electrical Performance of Li4Ti5O12 Anode Material for Lithium-Ion Batteries

Li4Ti5O12-based anode materials with low working potentials, high rate capabilities and high cyclability for high-power lithium-ion batteries: a synergistic effect of doping, incorporating a conductive phase and reducing the particle size

Al/Ti Synergistic Doping Enhanced Cycle Stability of Li‐Rich Layered Oxides

Zr/Ti Trace Co-Doping Induced Disordered Structure to Enhance the Cycling Stability of Li-rich Mn-based Layered Oxide Cathodes

Unraveling the Distinct Roles of Mg Occupation on Li or Co Sites on High-Voltage LiCoO<sub>2</sub>

Nitrogen and sulfur co-doped carbon-coated Li4Ti5O12 composite to enhance lithium storage properties

Zirconium(IV) Doping Enlarging Lithium-Ion Diffusion Channel of Lithium-Rich Li2.24SrTi6O14 Anode Material for High-Rate Lithium-Ion Batteries

Stabilizing 4.6 V LiCoO2 via Er and Mg Trace Doping at Li-Site and Co-Site Respectively