Zr/Ti Trace Co-Doping Induced Disordered Structure to Enhance the Cycling Stability of Li-rich Mn-based Layered Oxide Cathodes

Hong Zhang,Jianyue jiao,Ao Zen,Enyue Zhao,Jinkui Zhao,Xiaoling Xiao

DOI: https://doi.org/10.1016/j.electacta.2023.143167

IF: 6.6

2023-09-11

Electrochimica Acta

Abstract:Due to the ultrahigh energy density, Li-rich Mn-based layered oxide cathodes have attracted great attentions. However, the irreversible structural transformation usually leads to long-cycled capacity decay, which severely restricts their practical applications. Here, a Zr/Ti trace co-doping strategy is proposed to stabilize the structure and obtain excellent electrochemical performance by constructing bulk phase disorder and surface Zr-enriched structures. The designed Li 1.2 Mn 0.53 Ni 0.13 Co 0.13 Zr 0.005 Ti 0.005 O 2 (ZT-LRM) not only shows a higher specific capacity but also achieves an excellent long-cycle performance. The capacity retention of ZT-LRM is 69% after 500 cycles at 5C (1250 mA g −1 ), which is much higher than that (34%) of the Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 cathode. Neutron powder diffraction and transmission electron microscopy are used to demonstrate the disordered structure in the particles and the line scanning proves the surface Zr enrichment. In-situ X-ray diffraction verifies the more stable structural evolutions of the ZT-LRM during cycling. This simple modification method provides a reference for commercial applications of Li-rich Mn-based layered oxide cathodes.

electrochemistry