Novel Water-Assisting Low Firing MoO3 Microwave Dielectric Ceramics

Di Zhou,Li-Xia Pang,Da-Wei Wang,Ian M. Reaney

DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.01.052

IF: 5.7

2019-01-01

Journal of the European Ceramic Society

Abstract:MoO3 ceramics can not be well densified via conventional solid state method and a low relative density (rho) was obtained ((similar to)64.5% at 680 degrees C) with a permittivity (epsilon(r)) (similar to) 7.58, a quality factor (Qf) (similar to) 35,000 GHz and a temperature coefficient of resonant frequency (TCF)(similar to) - 39 ppm/degrees C. However, cold sintering at 150 degrees C using 4 wt. % H2O at 150 MPa enhanced densification and give a relative rho (similar to)76.8% and epsilon(r) (similar to) 8.31 but with a Qf of only (similar to) 900 GHz. The addition of (NH4)(6)Mo7O24 center dot 4H(2)O further improved densification to give a relative rho (similar to) 83.7% after annealing at 700 degrees C, resulting in a epsilon(r) (similar to) 9.91 with a Qf (similar to) 11,800 GHz. We conclude therefore that oxides that are difficult to be sintered via a conventional solid state route may benefit from cold sintering but despite the higher density, lower Qf cannot be avoided due to the impurities and grain boundary phases that are introduced.