Microwave dielectric properties of low firing (Na 0.5 Ln 0.5 )MoO 4 (Ln=Nd and Ce) ceramics

haihong xi,di zhou,huidong xie,wenbo li

DOI: https://doi.org/10.1016/j.ceramint.2014.12.124

IF: 5.532

2015-01-01

Ceramics International

Abstract:A new series of sheelite structured (Na(0.5)Ln(0.5))MoO4 (Ln=Nd and Ce) ceramics was prepared by using the traditional solid state reaction method. The (Na0.5Nd0.5)MoO4 ceramic could be well densified at 760 degrees C with excellent microwave dielectric properties (a permittivity of similar to 10.5, a quality factor Q x f of similar to 19,605 GHz (f=9.15 GHz) and a temperature coefficient of frequency of (TCF or tau(f))similar to 49 ppm/degrees C). Meanwhile, the (Na0.5Ce0.5)MoO4 ceramic sintered at 780 degrees C possessed the best microwave dielectric properties with a permittivity of similar to 11.2, a Q x f value of 19,365 GHz (f= 8.98 GHz) and TCF of approximately 44 ppm/degrees C. The (Na0.5Nd0.5)MoO4 ceramic was found to be chemically compatible with Ag electrode at its sintering temperature. It is a promising microwave dielectric material for low-temperature co-fired ceramic technology (LTCC). However, the (Na0.5Ce0.5)MoO4 ceramic was found to react with Ag after co-firing at 780 degrees C for 2 h and this limited its application in LTCC technology. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.