Novel Water Insoluble (Naxag2-X) Moo4 (0 <= X <= 2) Microwave Dielectric Ceramics with Spinel Structure Sintered at 410 Degrees

Di Zhou,Jing Li,Li-Xia Pang,Da-Wei Wang,Ian M. Reaney

DOI: https://doi.org/10.1039/c7tc01718a

IF: 6.4

2017-01-01

Journal of Materials Chemistry C

Abstract:In the present work, a novel series of water insoluble ultra-low temperature firing (Na,Ag)(2)MoO4 microwave dielectrics were prepared via the traditional solid state reaction method. A spinel structured solid solution was formed in the full composition range in the (NaxAg2-x)MoO4 (0 <= x <= 2). As x increased from 0 to 2.0, cell volume decreased linearly from 9.32 A to 9.10 A. Sintering behavior were described using a so-called 'bowing' effect and densification was achieved below 420 C for 0.5 <= x <= 1.2 with grain size, 1 to 5 mu m. Optimum microwave dielectric properties were obtained for (Na1.2Ag0.8)MoO4 ceramics sintered at 410 C with a permittivity similar to 8.1, a microwave quality factor similar to 44 800 GHz and the temperature coefficient of the resonant frequency similar to-82 ppm C-1 at 13.9 GHz. Silver within the solid solution inhibited hydrolyzation of ceramics and also reduced their sintering temperature. Compared with the sintering temperatures of traditional microwave dielectric ceramic (Al2O3, >1400 C) and normal low temperature co-fired ceramics (<960 C), this system will save lots of energy during processing and accelerate developments of sustainable electronic materials and devices.