Abstract:Temperature is one of the critical factors that strongly affect the behavior of hydrogen isotopes in tungsten (W). This work investigates the effect of initial exposure temperature on the deuterium (D) retention and surface blistering in recrystallized W. D plasma exposure is started at 420 K and 600 K, respectively, and then changed to the same temperature of 520 K. For each temperature, the irradiation fluence is ∼ 1 × 1026 D m−2, and therefore the total fluence is ∼ 2 × 1026 D m−2 for each sample. A reference W sample was also exposed at 520 K with the same total fluence. Compared with the reference sample, it is found that the initial temperature of 420 K significantly inhibits the formation of intergranular blisters and leads to a reduction of intragranular blisters in size. Although the initial temperature of 600 K facilitates the formation of intergranular blisters, the intergranular blister size is reduced. This is possibly related to the relatively higher concentration of trapped D over a large depth range as revealed by the TMAP simulation results, leading to the fact that intergranular cracks are more prone to propagate along sloping grain boundaries. Thermal desorption spectra results show that the initial exposure temperature of 420 K and 600 K reduce D retention by a factor of ∼ 56 % and ∼ 34 %, respectively. It is considered to be connected with the blistering-induced defects and D transport in W, which are strongly affected by the initial exposure temperature. This work demonstrates that the initial exposure temperature plays a crucial role in D behavior in W, improving the understanding of the temperature effects of hydrogen isotopes behavior in W.

Blistering and Helium Retention of Tungsten and 5% Chromium Doped Tungsten Exposed to 60keV Helium Ions Irradiation

Effect of Ti/Cr Additive on Helium Diffusion and Segregation in Dilute Vanadium Alloys

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Surface Blistering and D Desorption in High-Energy-rate Forging W, W-Y2O3, W-TiC Exposed to Deuterium Plasma

Retention and Thermal Desorption of Helium in Pure Tungsten

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Mechanisms of helium irradiation blistering and surface deformation in tungsten

Suppression of vacancy formation and hydrogen isotope retention in irradiated tungsten by addition of chromium

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Role of Helium Bubbles and Voids on the Property of Nanocrystalline Tungsten

Thermal conductivity and deuterium/helium plasma irradiation effect of WTaCrVTi high entropy alloy

Recovery and recrystallization of warm-rolled tungsten during helium thermal desorption spectroscopy annealing

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Effect of helium pre-implantation on the thermal shock performance of tungsten

Helium Radiation Blistering Mechanisms in Tungsten: Ion Channeling Effects

Effect of Surface Quality on Hydrogen/helium Irradiation Behavior in Tungsten

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten