Abstract:Surface damage and fuel retention are one of the major threats to the performance of plasma-facing materials (PFMs) in ITER and future fusion reactors. This work aims to investigate the influence of suppressed blistering by heavy ion pre-damage on deuterium (D) retention in tungsten (W). Recrystallized W samples were irradiated with 3.5 MeV iron (Fe13+) ions at room temperature to create displacement damage with a peak damage level of 0.1 dpa. Afterwards, a series of low-energy (38 eV) D plasma exposures were performed at 500 K. Three exposure fluences below and above the blistering threshold (5 x 10(24) similar to 3 x 10(25) D m(-2)) of the pre-damaged W are selected to decouple and couple the damage-induced defects and blistering-induced defects, respectively. Surface observations show that no blisters are formed in un-damaged W after low-fluence D exposure (5 x 10(24) D m(-2)), whereas severe blistering (surface coverage ratio: 34.2 %) occurs in the high-fluence case (3 x 10(25) D m(-2)). In contrast, only a small number of blisters (4.2 %) are formed in Fe-damaged W when D fluence reaches 3 x 10(25) D m(-2). Moreover, Fe pre-damage increases D retention by a factor of 3.33 and 1.20 at the low-fluence (5 x 10(24) D m(-2)) and medium-fluence (1 x 10(25) D m(-2)) D exposure, respectively. While in the high-fluence case (3 x 10(25) D m(-2)), the enhancement effect of D retention in Fe-damaged W is significantly weakened, such that retention is lower for damaged W, probably due to the significant suppression effect on surface blistering and its accompanying defect formation. This work highlights the suppressed blistering-induced D retention by pre-existing damage in W.

Decreased surface blistering and deuterium retention in potassium potassium-doped tungsten exposed to deuterium plasma following ion irradiation

Decreased Surface Blistering and Deuterium Retention in Potassium-Doped Tungsten Exposed to Deuterium Plasma Following Ion Irradiation

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Effect of potassium doping and exposure temperature on the deuterium behavior in large-scale potassium-doped tungsten

Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Aggravated Blistering and Increased Deuterium Retention in Iron-Damaged Tungsten after Exposure to Deuterium Plasma with Various Surface Temperatures

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Effect of Heavy Ion Pre-Irradiation on Blistering and Deuterium Retention in Tungsten Exposed to High-Fluence Deuterium Plasma

Deuterium Retention and Surface Blistering in Non-Damaged and Damaged Tungsten after Repetitive Plasma Exposure and Outgassing

Deuterium Distribution and Behavior of Blisters in Pre-Damaged and Undamaged Tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Suppression of Deuterium-Induced Blistering in Pre-Damaged Tungsten Exposed to Short-Duration Deuterium Plasma

Effect of Anisotropic Grain Boundaries on the Surface Blistering of Tungsten Induced by Deuterium Plasma Exposure

Influence of Suppressed Blistering by Heavy Ion Pre-Damage on Deuterium Retention in Tungsten

Irradiation hardening and deuterium retention behaviour of tungsten under synergistic irradiations of 3.5 MeV Fe 13+ ions and deuterium plasma

Surface Blistering and D Desorption in High-Energy-rate Forging W, W-Y2O3, W-TiC Exposed to Deuterium Plasma

Effect of Fe11+ Ion Combined with Helium and Deuterium Plasmas Irradiation on the Transient Thermal Shock Behaviors of Pure and Potassium-Doped Tungsten

Irradiation Hardening and Deuterium Retention Behaviour of Tungsten under Synergistic Irradiations of 3.5 MeV Fe13+ Ions and Deuterium Plasma

The Effect of Pre-Damage Distribution on Deuterium-Induced Blistering and Retention in Tungsten

Effect of 3 MeV Fe<SUP>11+</SUP> ions pre-damage on blistering and deuterium retention in two tungsten grades