Abstract:Temperature is one of the critical factors that strongly affect the behavior of hydrogen isotopes in tungsten (W). This work investigates the effect of initial exposure temperature on the deuterium (D) retention and surface blistering in recrystallized W. D plasma exposure is started at 420 K and 600 K, respectively, and then changed to the same temperature of 520 K. For each temperature, the irradiation fluence is ∼ 1 × 1026 D m−2, and therefore the total fluence is ∼ 2 × 1026 D m−2 for each sample. A reference W sample was also exposed at 520 K with the same total fluence. Compared with the reference sample, it is found that the initial temperature of 420 K significantly inhibits the formation of intergranular blisters and leads to a reduction of intragranular blisters in size. Although the initial temperature of 600 K facilitates the formation of intergranular blisters, the intergranular blister size is reduced. This is possibly related to the relatively higher concentration of trapped D over a large depth range as revealed by the TMAP simulation results, leading to the fact that intergranular cracks are more prone to propagate along sloping grain boundaries. Thermal desorption spectra results show that the initial exposure temperature of 420 K and 600 K reduce D retention by a factor of ∼ 56 % and ∼ 34 %, respectively. It is considered to be connected with the blistering-induced defects and D transport in W, which are strongly affected by the initial exposure temperature. This work demonstrates that the initial exposure temperature plays a crucial role in D behavior in W, improving the understanding of the temperature effects of hydrogen isotopes behavior in W.

Effect of potassium doping and exposure temperature on the deuterium behavior in large-scale potassium-doped tungsten

Decreased Surface Blistering and Deuterium Retention in Potassium-Doped Tungsten Exposed to Deuterium Plasma Following Ion Irradiation

Decreased surface blistering and deuterium retention in potassium potassium-doped tungsten exposed to deuterium plasma following ion irradiation

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Dependence of deuterium retention and surface blistering on deuterium plasma exposure temperature and fluence in lanthanum oxide doped tungsten

Effect of potassium bubbles on the thermal shock fatigue behaviors of large-volume potassium-doped tungsten alloy

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Effect of Potassium Doping on the Thermal Shock Behavior of Tungsten

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Surface Blistering and D Desorption in High-Energy-rate Forging W, W-Y2O3, W-TiC Exposed to Deuterium Plasma

Deuterium Retention and Surface Blistering in Non-Damaged and Damaged Tungsten after Repetitive Plasma Exposure and Outgassing

Effect of Exposure Temperature on Deuterium Retention and Surface Blistering of Tungsten Exposed to Sequential Nitrogen and Deuterium Plasma

Influence of Suppressed Blistering by Heavy Ion Pre-Damage on Deuterium Retention in Tungsten

Deuterium Distribution and Behavior of Blisters in Pre-Damaged and Undamaged Tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Tungsten–potassium: a Promising Plasma-Facing Material

Surface Blistering and Deuterium Retention in Tungsten Exposed to Low-Energy Deuterium Plasma at Different Temperatures