X-ray Microscopic and Thermodynamic Model Assessments of Softening in TIG-Welded AA 6061-T651
Muhammad Zia ud din Urf Umer,Ahmed A. Tiamiyu
DOI: https://doi.org/10.1007/s11665-024-09452-0
IF: 2.3
2024-04-28
Journal of Materials Engineering and Performance
Abstract:Fusion welding is extensively used for joining structural assemblies, especially those with complex geometries. However, it often results in heat-affected zones (HAZ) that are, in most cases, softer than other regions around and beyond the weld area. Coupling both experiment and thermodynamic modeling—electron microscopy, x-ray microscopy (XRM), and CALculation of PHAse Diagrams (CALPHAD)—we re-examine the origin of softening in tungsten inert gas (TIG)-welded heat-treatable AA 6061-T651 for a more comprehensive understanding of its (softening) evolution. This study reveals material softening up to at least 38 mm away from the weld center, and partitioned heat-affected zones—HAZ1, HAZ2, HAZ3, and HAZ4—based on peak temperature, associated hardness, and precipitate phases in these zones. Analytical modeling and thermodynamic simulation predict solid solution and further precipitation of coherent GP zones in HAZ1, while coarsening of pre-existing precipitate occurs in HAZ2 (non-coherent/stable β -Mg 2 Si), HAZ3 (both semi-coherent/metastable β ′ and coherent/metastable β ′′) and HAZ4 (coherent/metastable β ′′). These welding-induced transformations—origin of softening—result in non-homogenous hardness in the zones compared to the unaffected base material (120 HV): HAZ1 to HAZ4 are 66-72, 54-64, 64-94, and 95-106 HV, respectively. Under tensile load, the TIG-welded sample fractures at the softest region—HAZ2. Additionally, XRM analysis confirms the presence of porosity in the welded area and its closure during plastic deformation, so that the severity of softening has a greater influence on localized fracture than the presence of porosity in the weld area. This work shows that new solid-state welding technologies that minimize nanostructural changes in base materials, especially precipitation-hardened alloys, should be sought.
materials science, multidisciplinary