Enhanced Dielectric, Electromechanical and Hydrophobic Behaviors of Core-Shell AgNWs@SiO2/PDMS Composites

Zhou,Hao Wang,Zhicai Zhu,Hui Yang,Qilong Zhang

DOI: https://doi.org/10.1016/j.colsurfa.2018.11.067

IF: 5.518

2019-01-01

Colloids and Surfaces A Physicochemical and Engineering Aspects

Abstract:This paper reports a feasible method to prepare polymeric nanocomposites with enhanced dielectric, electromechanical and hydrophobic performance by introducing the core-shell AgNWs@SiO2 filler into poly-dimethylsiloxane (PDMS). The homogenous core-shell AgNWs@SiO2 was firstly synthesized through a two-step sol-gel process. The thicknesses of AgNWs and SiO2 coating layer are approximately 70 nm and 20 nm, respectively. The dielectric constant is improved effectively due to enhanced interfacial polarization, while extremely low dielectric loss and conductivity are achieved by introducing the insulating SiO2 interlayer to moderate the internal surface area of core-shell nanowires and restrict the electron transfer between Ag nano-wires. Typically, the PDMS nanocomposites with 20 wt% AgNWs@SiO2 have a dielectric constant of 6.7, nearly 2.7 times larger than that of pure PDMS, and remains a quite low loss of 0.02 at 1 kHz. Meanwhile, nanocomposites also show improved electromechanical and hydrophoic properties. Nanocomposites with 10 wt% AgNWs@SiO2 exhibit the highest electromechanical sensitivity (beta=9.04), about 12.6 times higher than that of pure PDMS at 1 kHz. The static contact angle of nanocomposties with 20 wt% AgNWs@SiO2 reaches 129 degrees. All the improved performances show great potential application for dielectric elastomer material and electrowetting devices.