Preparation and Enhanced Dielectric-hydrophobic Properties of PDMS-PVDF Composite Films with Au@PS Nanoparticle

Zhang Qilong,Yao Liqin,Zhu Zhicai,Zhang Zhao,Yang Hui

DOI: https://doi.org/10.7503/cjcu20200102

2020-01-01

Abstract:Au nanoparticles were uniformly loaded on the surface of polystyrene ( PS) microspheres with an average diameter about 250 nm via the emulsion polymerization and reduction method. The PS/Au was homogeneously mixed with polydimethylsiloxane (PDMS)/poly (vinylidene fluoride-co-trifluoroethylene) [P(VDF-TrFE)](mass ratio ; 2 3) by solution blending method, and the dense composite film with uniform distribution of Au@ PS particle and micro bulge surface were obtained. The effects of Au@ PS doping content on composite films structure, melting crystallization behavior and dielectric-hydrophobic properties were investigated. It was found that the introduction of Au@ PS nanoparticles hinders the beta phase formation of P (VDF-TrFE), but has no obvious effect on the bonding structures. The crystallization temperature and glass-transition temperature of composite films increases, and their melting point decreases slightly with increasing the Au@ PS content. Due to the synergistic effect of interface polarization and micro capacitance, the dielectric constant of composite film with Au@ PS nanoparticles is significantly increased. The Au nanoparticles uniformly loaded on the surface of PS sphere reduce the formation of conductive network, thus maintain a relatively low dielectric loss value. Typically, the dielectric constant of the blend film with 5% (mass fraction) Au@ PS nanoparticle reaches 22 at 100 Hz, which is 8. 8 and 3. 14 times that of pure PDMS and PDMS/P (VDF-TrFE), respectively. The blend film with 5%Au@ PS also possesses a large contact angle of 112. 31 degrees due to the interaction of hydrophilic Au nanoparticles and the existence of micro bulge structure. All the improved performances show great potential application for electrowetting devices.