Abstract:The precipitates in a Mg-7Gd-5Y-1Nd-0.5Zr alloy aged to peak-ageing plateau (aged at 210 degrees C from 18 h to 180 h) were studied using transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). Precipitation at the peak-ageing plateau involves the formation of the beta' phase and a new type of plate-shaped phase precipitated along the (0 0 0 1)(alpha) habit plane. The ellipsoid morphology of beta' was illustrated according to [0 0 0 1](alpha) and [1 0 (1) over bar 0](alpha) zone axes observations. The orientation relationship between the beta' precipitates and matrix satisfies [0 0 1](beta')//[0 0 0 1](alpha) and (1 0 0)(beta')//(1 1 (2) over bar 0)(alpha), respectively. The TEM and HRTEM results indicate that the beta' precipitates have a base-centred orthorhombic structure with lattice parameters a = 0.64 nm, b = 2.22 nm and c = 0.52 nm. Further, atomic-scaled HAADF-STEM observations suggest a Mg7RE-type and not a Mg15RE-type structure for the beta' phase. The positive thermal stability of the alloy at 210 degrees C ageing is attributed to the coherent relationship with the matrix and the formation of an interlaced network of the beta' precipitates. Aside from the beta' phase, a large amount of precipitate particles were observed to form on the (0 0 0 1)(alpha) habit plane in the peak-aged samples. The new type of precipitates have a plate shape, of approximately 5 nm wide along the [1 0 (1) over bar 0](alpha) direction of the matrix and approximately 5 nm long along the [(2) over bar 1 1 0](alpha) direction. A completely coherent relationship with the matrix can also be observed. (c) 2013 Elsevier B.V. All rights reserved.

On the Evolution of Β' Precipitate During Creep in a Mg–3.3Y–0.1Zr(at.%) Alloy

Tensile Creep Behavior and Microstructure Evolution of Mg-11Gd-2Y-0.5Zr Alloy

A Simulation Study of the Distribution of Β′ Precipitates in a Crept Mg-Gd-Zr Alloy

Linear Precipitate Chains in Mg-2.4Gd-0.1Zr Alloy after Creep

Formation Of The Creep-Induced Beta(2) Phase And Its Influence On Deformation In A Fully-Lamellar Tial Alloy

Adjustment of a Novel Β′-Type Precipitate in a Creep-Aged Mg−15 Wt%gd Alloy

Evolution Process of Precipitate-Free Zones in a Mg-Gd Alloy During Creep

Microstructural evolution of Mg–14Gd–0.4Zr alloy during compressive creep

Effect of Dynamic Precipitation on Creep Behavior of Mg-5zn-2al(-2y) Alloy

Alignment and Strengthening Effect of Β′ Precipitates in Mg-Gd-Y-Zr During Ageing Process Studied by HAADF-STEM and GPA

Characterisation of Precipitates in a Mg–7Gd–5Y–1Nd–0.5Zr Alloy Aged to Peak-Ageing Plateau

Characterization of β precipitate phase in Mg-7Gd-5Y-1Nd-0.5Zr alloy

Abnormal creep behavior of Mg-12Gd-1MM-0.6Zr (wt.%) alloy at 300C

Creep Behavior and Precipitation Evolution of Mg-13Gd-2y-0.5zr Alloy

Unveiling the Collaborative Effects of Static Precipitation and Precipitate-Free Zone on the Compressive Creep Behaviors of Mg-10.5wt%Y Binary Alloy

Research on Dynamic Precipitation Behavior of Pre-Solution Treated Mg–5 Wt.% Zn–2 Wt.% Al(–2 Wt.%y) Alloy During Creep

Compressive creep behavior of extruded Mg-4Sm-2Yb-0.6Zn-0.4Zr alloy

On the Evolution of Β1/β' Coupled-Structures in Mg–Y–Nd Alloys: A Simulation Study

On the Strengthening Precipitate Phases and Phase Transformation of Β″/β′ in a Mg-Sm-Zr Alloy

Precipitate Phases in the Mg-4Y-4Sm-0.5Zr Alloy

Creep Behavior and Related Phase Precipitation of a Creep-Resistant Y2O3-bearing High Nb Containing TiAl Alloy