Adjustment of a Novel Β′-Type Precipitate in a Creep-Aged Mg−15 Wt%gd Alloy

Zefeng Xie,Qiang Yang,Shuhui Lv,Bo Deng,Wei Sun,Xin Qiu

DOI: https://doi.org/10.1016/j.msea.2023.145982

2024-01-01

Abstract:A Mg-15 wt%Gd binary alloy was prepared by hot-extrusion and then creep-aged at 200 degrees C under a constant stress of 200 MPa in this work. Compared with the traditional aging, creep aging clearly accelerated the age-hardening response, as the aging time for the peak yield strength was shorten from 72h to similar to 16h. In the peak-creep-aged sample, a novel precipitation structure, named as beta '(H) herein, was observed as the dominant precipitate. Interestingly, these dense beta '(H) precipitates preferred to distributing along a certain direction which generally deviated from the extrusion direction (ED) by 54-67 degrees. Aberration-corrected high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) characterization revealed that this novel beta '(H) precipitate is composed of distorted Gd-rich hexagonal units, with the chemical formula of Mg7Gd2 and having a monoclinic structure, a = 0.671 nm, b = 1.727 nm, c = 0.521 nm and beta = 100.7 degrees. Density functional theory (DFT) calculations suggest that the applied stress during creep aging could provide an effective tensile stress for the motion of the surrounding Mg atoms when forming the beta '(H) structure.