Precipitate Phases in the Mg-4Y-4Sm-0.5Zr Alloy

Daquan Li,Qudong Wang,Wenjiang Ding

DOI: https://doi.org/10.1016/j.jallcom.2007.10.081

IF: 6.2

2008-01-01

Journal of Alloys and Compounds

Abstract:Precipitate phases in the Mg-4Y-4Sm-0.5Zr alloy have been characterised using TEM. The precipitation sequence in the Mg-4Y-4Sm-0.5Zr alloy involves formation of phases as β′-β1-β. The β′ precipitates were formed within the grains when the alloy was aged at 473K. This intermediate β′ phase is thermally stable at 473K. The globular shape β′ precipitates were formed in the under aged state at 473K. These globular shape β′ precipitates coalesced, and the plate shape β′ precipitates were formed lying in the {21¯1¯0} habit planes with increasing ageing time. The much bigger equilibrium β precipitates with fcc crystal structure were directly precipitated on the grain boundaries at 473K. The β1 precipitates were formed within the grains when the alloy was aged at 523K. These plate shape β1 precipitates lied in the {101¯0} habit plane and in contact with β′ precipitates. The plate shape equilibrium β precipitates with fcc crystal structure precipitated along the {101¯0} habit plane when the alloy was aged at 573K. The orientation relationship between β and the Mg matrix is: [111]β||[21¯1¯0]a, (2¯20)β||(0001)a.