Abstract:The precipitates in a Mg-7Gd-5Y-1Nd-0.5Zr alloy aged to peak-ageing plateau (aged at 210 degrees C from 18 h to 180 h) were studied using transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). Precipitation at the peak-ageing plateau involves the formation of the beta' phase and a new type of plate-shaped phase precipitated along the (0 0 0 1)(alpha) habit plane. The ellipsoid morphology of beta' was illustrated according to [0 0 0 1](alpha) and [1 0 (1) over bar 0](alpha) zone axes observations. The orientation relationship between the beta' precipitates and matrix satisfies [0 0 1](beta')//[0 0 0 1](alpha) and (1 0 0)(beta')//(1 1 (2) over bar 0)(alpha), respectively. The TEM and HRTEM results indicate that the beta' precipitates have a base-centred orthorhombic structure with lattice parameters a = 0.64 nm, b = 2.22 nm and c = 0.52 nm. Further, atomic-scaled HAADF-STEM observations suggest a Mg7RE-type and not a Mg15RE-type structure for the beta' phase. The positive thermal stability of the alloy at 210 degrees C ageing is attributed to the coherent relationship with the matrix and the formation of an interlaced network of the beta' precipitates. Aside from the beta' phase, a large amount of precipitate particles were observed to form on the (0 0 0 1)(alpha) habit plane in the peak-aged samples. The new type of precipitates have a plate shape, of approximately 5 nm wide along the [1 0 (1) over bar 0](alpha) direction of the matrix and approximately 5 nm long along the [(2) over bar 1 1 0](alpha) direction. A completely coherent relationship with the matrix can also be observed. (c) 2013 Elsevier B.V. All rights reserved.

Hrtem Studies of Aging Precipitate Phases in the Mg-10gd-3y-0.4zr Alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Characterization of β precipitate phase in Mg-7Gd-5Y-1Nd-0.5Zr alloy

Characterization and Strengthening Effect of Precipitate Microstructure in Mg-3nd-3gd-0.2zn-0.5zr Alloy Aged at 225 °C

Precipitation Microstructure and Age-Hardening Response of an Mg–Gd–Nd–Zn–Zr Alloy

A New Metastable Precipitate Phase in Mg–Gd–Y–Zr Alloy

Novel structures observed in Mg–Gd–Y–Zr during isothermal ageing by atomic-scale HAADF-STEM

Precipitation in a Mg–10Gd–3Y–0.4Zr (wt.%) Alloy During Isothermal Ageing at 250 °C

Mechanical Properties and Microstructure Evolution of Mg-Gd Alloy During Aging Treatment

Microstructure Evolution in a Mg–15Gd–0.5Zr (wt.%) Alloy During Isothermal Aging at 250°C

Precipitate Evolution in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr Alloy During Isothermal Ageing at 240 °C

Early stages of precipitation and microstructure control in Mg–rare earth alloys

Microstructure and Mechanical Properties of a Cast Heat-Resistant Rare-Earth Magnesium Alloy

Precipitation and its effect on the mechanical properties of a cast Mg–Gd–Nd–Zr alloy

Effect of aging temperature on the hardening behavior and precipitation evolution of Mg 10Gd alloy

A Detailed HAADF-STEM Study of Precipitate Evolution in Mg–Gd Alloy

Precipitation Processes During the Peak-Aged and Over-Aged Stages in an Mg-Gd-Y-Zr Alloy

Precipitation behaviors and mechanical properties of Mg-6Gd-Y-0.6Zr alloy

Isochronal Aging Hardening of the Mg-8Gd-3Y-0.5Zr Alloy after Cold Rolling

Characterisation of Precipitates in a Mg–7Gd–5Y–1Nd–0.5Zr Alloy Aged to Peak-Ageing Plateau

Precipitation and Its Effect on Age-Hardening Behavior of As-Cast Mg–Gd–Y Alloy