Abstract:The precipitates in a Mg-7Gd-5Y-1Nd-0.5Zr alloy aged to peak-ageing plateau (aged at 210 degrees C from 18 h to 180 h) were studied using transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and high-angle annular detector dark-field scanning transmission electron microscopy (HAADF-STEM). Precipitation at the peak-ageing plateau involves the formation of the beta' phase and a new type of plate-shaped phase precipitated along the (0 0 0 1)(alpha) habit plane. The ellipsoid morphology of beta' was illustrated according to [0 0 0 1](alpha) and [1 0 (1) over bar 0](alpha) zone axes observations. The orientation relationship between the beta' precipitates and matrix satisfies [0 0 1](beta')//[0 0 0 1](alpha) and (1 0 0)(beta')//(1 1 (2) over bar 0)(alpha), respectively. The TEM and HRTEM results indicate that the beta' precipitates have a base-centred orthorhombic structure with lattice parameters a = 0.64 nm, b = 2.22 nm and c = 0.52 nm. Further, atomic-scaled HAADF-STEM observations suggest a Mg7RE-type and not a Mg15RE-type structure for the beta' phase. The positive thermal stability of the alloy at 210 degrees C ageing is attributed to the coherent relationship with the matrix and the formation of an interlaced network of the beta' precipitates. Aside from the beta' phase, a large amount of precipitate particles were observed to form on the (0 0 0 1)(alpha) habit plane in the peak-aged samples. The new type of precipitates have a plate shape, of approximately 5 nm wide along the [1 0 (1) over bar 0](alpha) direction of the matrix and approximately 5 nm long along the [(2) over bar 1 1 0](alpha) direction. A completely coherent relationship with the matrix can also be observed. (c) 2013 Elsevier B.V. All rights reserved.

A New Metastable Precipitate Phase in Mg–Gd–Y–Zr Alloy

Hrtem Studies of Aging Precipitate Phases in the Mg-10gd-3y-0.4zr Alloy

Novel structures observed in Mg–Gd–Y–Zr during isothermal ageing by atomic-scale HAADF-STEM

Precipitation in Mg-Gd-Y-Zr Alloy: Atomic-scale Insights into Structures and Transformations

Unveiling precipitation behavior in Mg-Y based alloys

The Formation Mechanism of a Novel Interfacial Phase with High Thermal Stability in a Mg-Gd-Y-Ag-Zr Alloy

Characterization of β precipitate phase in Mg-7Gd-5Y-1Nd-0.5Zr alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

On the Strengthening Precipitate Phases and Phase Transformation of Β″/β′ in a Mg-Sm-Zr Alloy

A Detailed HAADF-STEM Study of Precipitate Evolution in Mg–Gd Alloy

Precipitation in a Mg–10Gd–3Y–0.4Zr (wt.%) Alloy During Isothermal Ageing at 250 °C

Characterisation of Precipitates in a Mg–7Gd–5Y–1Nd–0.5Zr Alloy Aged to Peak-Ageing Plateau

Precipitation Behavior of Mg-7Gd-3Y-2Zn-0.5Zr Alloy during Isothermal Aging

Segregation of Rare Earth Atoms in Mg-Gd-Y-Zr Alloy after a 6-Year Natural Ageing at Room Temperature: Atomic-scale Direct Imaging

Atomic-scale Insights on the Plate-Shaped Γ″ Phase in Mg–Gd–Y–Ag–Zr Alloy

Precipitate Evolution in Mg−7Gd−3Y−1Nd−1Zn−0.5Zr Alloy During Isothermal Ageing at 240 °C

Precipitation of Secondary Phase in Mg-Zn-Gd Alloy after Room-Temperature Deformation and Annealing

Precipitation Process in a Mg–Gd–Y Alloy Grain-Refined by Al Addition

Revisiting the evolution behaviors of β ' phase in Mg-Nd and Mg-Y alloys

Microstructure and Mechanical Properties of Mg-12gd-2y-1sm-0.5zr Alloy

Morphology and crystallography of β precipitate phase in Mg-Gd-Y-Nd-Zr alloy