Deformation mechanisms in a novel multiscale hetero-structured Mg alloy with high strength-ductility synergy
Tong Wang,Min Zha,Yipeng Gao,Si-Qing Wang,Hai-Long Jia,Cheng Wang,Hui-Yuan Wang
DOI: https://doi.org/10.1016/j.ijplas.2023.103766
IF: 8.5
2023-09-01
International Journal of Plasticity
Abstract:Most of the high-strength Mg alloys exhibit poor ductility at room temperature. Architecturing appropriate heterostructure in metallic materials gives rise to the breakthrough of the inherent strength-ductility trade-off dilemma. Here, we prepared a novel multiscale hetero-structure in Mg-9Al-1 Zn (AZ91) alloy, consisting of bimodal-structured center-region and fine-grained surface-layer, providing high strength and high ductility, i.e. yield strength of ∼303 MPa, tensile strength of ∼400 MPa, and elongation of ∼14.5 %. The multiscale microstructural heterogeneities were induced via a simple rolling process that combines the advantages of both accumulative rolling bonding (ARB) and hard plate rolling (HPR). By utilizing quasi-in-situ electron backscattered diffraction (EBSD)-digital image correlation (DIC) characterizations combined with the determination of dislocation/disclination distributions, it has been found that diversified strain accommodation mechanisms are stimulated by the strain incompatibilities near hetero-interfaces in the multiscale hetero-structure. In particular, non-basal slips have been activated largely in both the bimodal-structured center-region and fine-grained surface-layer. Moreover, a unique slip trace distribution has been observed in the fine grains adjacent to the basal-oriented coarse grain. Such a strain accommodation can better coordinate local strain incompatibility among the hetero-interface. The uniaxial loading–unloading–reloading tensile loop tests demonstrate that the multiscale heterogeneities impart a pronounced hetero-deformation induced hardening during tensile deformation. Multiple deformation modes, including the non-Schmid and non-basal slips, have been activated substantially in the multiscale hetero-structured Mg alloy, effectively relaxing local stress concentration and achieving stable plastic flow at a high-stress state, which is beneficial to improving strain-hardening ability and strength-ductility synergy. Our work could shed light on designing and processing strong and ductile Mg alloys, by tailoring proper microstructural heterogeneity to activate cooperated accommodating deformation modes.
materials science, multidisciplinary,engineering, mechanical,mechanics