Abstract:Currently, the hot forming of aluminum alloys has garnered significant attention for overcoming poor formability at room temperature (RT). However, the current hot forming technique is facing problems such as time-consuming procedures and high economic cost. To improve forming efficiency, we herein propose a novel forming technique for heat-treatable aluminum alloys, termed pre-aged hardening warm forming (PHF) process. An Al–Zn–Mg–Cu alloy is used to investigate the flow behavior, drawing formability, and post-forming mechanical properties during the aforementioned process. Uniaxial tensile tests and Erichsen tests are conducted to evaluate the plastic flow behavior and drawability, respectively. Stamping tests are performed on a cap beam component to verify the engineering feasibility of the forming technique. Optical microscopy (OM) and transmission electron microscopy (TEM) are performed to characterize the microstructure evolution during the PHF process. The tensile test results show that the pre-aged alloys exhibit true fracture elongation similar to the fracture elongation of the O-temper alloy at RT, and that the Erichsen values of the pre-aged alloys are 5%–16% higher than that of the O-temper alloy at 200 °C. The results of the stamping tests for the cap beam component indicate that the optimal final strength of the stamped component achieves σ/σ0.2 = 566 MPa/500 MPa, exceeding the strength of the AA7075-T6 alloy. OM observations show that the stamping process does not significantly affect the grain sizes of the pre-aged alloys. TEM results show that numerous thermostable GPⅡ zones exist in the pre-aged alloys, and that the stamping procedure transforms the GPⅡ zones to dispersed η′ phases and results in the entanglement of numerous dislocations. The dual effects of phase transformation and plastic deformation during the PHF process contribute to the desirable mechanical properties of the stamped components.

An Experimental Investigation on the Deformation and Post-Formed Strength of Heat-Treatable Aluminium Alloys Using Different Elevated Temperature Forming Processes

The Effect of Hot Form Quench (HFQ®) Conditions on Precipitation and Mechanical Properties of Aluminium Alloys

An Experimental Investigation of the Drawability of AA6082 Sheet under Different Elevated Temperature Forming Processes

Experimental Investigation of Forming Limit Curves and Deformation Features in Warm Forming of an Aluminium Alloy

Deformation Behavior and Mechanical Properties of AA7075 During Pre-hardened Aluminum Alloy Hot Forming Process

Investigation of formability, microstructures and post-forming mechanical properties of heat-treatable aluminum alloys subjected to pre-aged hardening warm forming

Comparative study on deformation behavior, microstructure evolution and post-forming property of an Al Zn Mg Cu alloy in a novel warm forming process

Experimental and Numerical Investigation on Strengthening Behavior of 7075 Aluminum Alloy Sheets in Hot Forming–Quenching Integrated Process

An Experimental and Numerical Investigation on the Formability of AA7075 Sheet in Hot Stamping Condition

Study on High-Temperature Mechanical Properties and Forming Limit Diagram of 7075 Aluminum Alloy Sheet in Hot Stamping

Modeling mechanical properties and plastic strain for hot forming-quenching AA6061 aluminum alloy parts

Hot Forming-Quenching Integrated Process with Cold-Hot Dies for 2a12 Aluminum Alloy Sheet

Investigation and Modeling of the Preheating Effects on Precipitation and Hot Flow Behavior for Forming High Strength AA7075 at Elevated Temperatures

Investigation of formability of aluminum alloy sheet at elevated temperature

Review of Hot Forming-quenching Integrated Process of Aluminum Alloy

Constitutive modelling of plastic deformation behaviour for AA7075-H18 alloy based on hot forming and in-die quenching (HFQ®) process

Strengthening Behavior of Al–Cu–Mg Alloy Sheet in Hot Forming–quenching Integrated Process with Cold–hot Dies

The Effect of Hot Forming–Quenching and Heat Treatment Processes on the Mechanical Properties of AA6016 Aluminum Alloy Sheets

Investigations into Hot Form Quench Conditions on Microstructure Evolution and Bake-Hardening Response for High-Strength Aluminum Alloy

Effect of Thermo-Mechanically Activated Precipitation on the Hot Deformation Behavior of High Strength Aluminum Alloy AA7075

Formability Evaluation of Aluminum Alloy 6061-T6 Sheet at Room and Elevated Temperatures