Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Strengthening Behavior of Al–Cu–Mg Alloy Sheet in Hot Forming–quenching Integrated Process with Cold–hot Dies

Experimental and Numerical Investigation on Strengthening Behavior of 7075 Aluminum Alloy Sheets in Hot Forming–Quenching Integrated Process

Wrinkling and Strengthening Behaviors in the Two-Layer-Sheet Hot-Forming–Quenching Integrated Process for an Al–Cu–Mg-Alloy Thin-Walled Curved-Surface Shell

Comparative study on deformation behavior, microstructure evolution and post-forming property of an Al Zn Mg Cu alloy in a novel warm forming process

Strength and Formability Improvement of Al-Cu-Mn Aluminum Alloy Complex Parts by Thermomechanical Treatment with Sheet Hydroforming

Comparative study on the formability and microstructure evolution of different tempered Al–Cu–Li alloy sheets during room and cryogenic temperature forming process

Coordinated deformation mechanisms of high formability Al–Mg–Si–Cu–Zn–Fe alloys via coupling control of thermomechanical processes

Investigation of the Hot Stamping-in-Die Quenching Composite Forming Process of 5083 Aluminum Alloy Skin

Hot Deformation Behavior and Processing Maps of an As-Cast Al-5Mg-3Zn-1Cu (wt%) Alloy

Effect of Heat Treatment Conditions on Mechanical Properties and Precipitates in Sheet Metal Hot Stamping of 7075 Aluminum Alloy

Study on High-Temperature Mechanical Properties and Forming Limit Diagram of 7075 Aluminum Alloy Sheet in Hot Stamping

Investigation of formability, microstructures and post-forming mechanical properties of heat-treatable aluminum alloys subjected to pre-aged hardening warm forming

Investigation on strengthening of 7075 aluminum alloy sheet in a new hot stamping process with pre-cooling

Modeling mechanical properties and plastic strain for hot forming-quenching AA6061 aluminum alloy parts

Investigation on effect of high-efficiency solid solution and hot stamping process on microstructure evolution and mechanical properties of high-strength aluminum alloy

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Application of Combined W-Temper and Cold Forming Technology to High-Strength Aluminum Alloy Automotive Parts

Deformation Behavior and Mechanical Properties of AA7075 During Pre-hardened Aluminum Alloy Hot Forming Process

The Effect of Hot Forming–Quenching and Heat Treatment Processes on the Mechanical Properties of AA6016 Aluminum Alloy Sheets

Mechanisms and microstructures of 2A97 Al-Li alloy under the hot forming with synchronous quenching process

A strategy to promote formability, production efficiency and mechanical properties of Al–Mg–Si alloy