Abstract:Surface modification and deuterium (D) retention in pure tungsten (W) and tungsten-rhenium (W-Re) alloys with Re concentration of 1, 3, 5 and 10 wt.% were investigated after exposure to D plasma with an incident energy of 38 eV/D at about 400 K and various fluences ranging from 7.2 × 1023 to 2.6 × 1025 D/m2. It is found that blistering depends strongly on the exposure fluence for both W and W-Re alloy samples. When the D fluence is higher than 2.8 × 1024 D/m2, the surface of W is covered by two types of blisters. One type is small blisters (<2 μm), which appeared in groups only on grains with surface orientation close to (111). The other type is large-sized (>8 μm) and extents over several grains. In the cases of W-Re alloys, only small blisters can be observed on their surface. The blisters on the surface of W-Re alloys preferentially appeared on grains with surface orientation close to (111). Cross-section views of blisters show that the blisters on W-Re alloys always originate from intra-granular cavities. The small and large blisters on W originate from intra- and inter-granular cavities, respectively. The surface blistering fluence threshold for W-Re alloys is lower than for W. For both types of materials, rupture of blisters occurs if the underlying crack reaches the surface at the edge of a blister. The number of ruptured blisters increases with increasing D fluence. TDS results show that there is an additional high-temperature peak at ∼ 800 K in W-Re alloys. The amount of D released from W and W-Re alloys increases with increasing D fluence. In addition, the accumulation of D in W-Re alloys is not noticeably influenced by the amount of Re doping at the exposure temperature of ∼ 400 K.

$\Langle 0\,0\,{\rm 1}\rangle $ Edge Dislocation Nucleation Mechanism of Surface Blistering in Tungsten Exposed to Deuterium Plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Mechanism for Orientation Dependence of Blisters on W Surface Exposed to D Plasma at Low Temperature

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Effect of thickness on the blistering of tungsten exposed to deuterium plasma

Nucleation Mechanism of Intra-Granular Blisters in Tungsten Exposed to Hydrogen Plasma

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Dependence of blistering and deuterium retention on damage depth in damaged tungsten exposed to deuterium plasma

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Blister-dominated retention mechanism in tungsten exposed to high-fluence deuterium plasma

Observations of Orientation Dependence of Surface Morphology in Tungsten Implanted by Low Energy and High Flux D Plasma

Surface Blistering and Deuterium Retention in Chemical Vapor Deposition Tungsten Exposed to Deuterium Plasma

Growth Mechanism of Subsurface Hydrogen Cavities in Tungsten Exposed to Low-Energy High-Flux Hydrogen Plasma

Dependence of deuterium retention and surface blistering on deuterium plasma exposure temperature and fluence in lanthanum oxide doped tungsten

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Surface modification and deuterium retention of tungsten and tungsten-rhenium alloys exposed to deuterium plasma