Abstract:Mg(BH4)2 was previously studied as a promising hydrogen storage material, because of its high gravimetric storage capacities for hydrogen and suitable thermodynamic properties. Mg(BH4)2 began to decompose at about 300 ℃, and formed MgB2 at the end of hydrogen desorption process with the weight content of 14.9% of hydrogen lost. Aside from the prominent hydrogen storage property, the decomposition process from Mg(BH4)2 to MgB2 can be a potential method for fabricating superconducting MgB2 at a low sintering temperature. In this paper, MgB2 bulk was prepared by an in-situ reaction, using the Mg(BH4)2 pressed block as a precursor. The resistance change of the sample was monitored during the Mg(BH4)2 decomposition process and the resistance-temperature (R-T) curve of this process was recorded. Phase of MgH2, Mg and B were formed as the block slowly release its hydrogen before MgB2 occurred. According to the R-T curve, the phase formation of MgB2 started in a relatively low temperature of 410 ℃. Because MgB2 was critically formed by Mg and B derived from Mg(BH4)2, we can compare our formation temperature with previous study on MgB2 prepared by Mg and B in different particle size. The fitting result indicated that the particle size of Mg and B harvest from Mg(BH4)2 decomposition was only 3.4 nm on average. The nearly atomic level mixture of Mg and B resulted in a high chemical reactivity, which was the main reason for low sintering temperature. X-ray diffraction results showed that the purity of MgB2 was 95.2%, and the size of MgB2 grains was 10–18 nm. SEM images showed that the MgB2 bulk had a porous structure and poor connectivity, which was caused by large amount the hydrogen release during the decomposition. MgB2 nanofibers can also be observed inside the bulk. In the superconductivity test, the superconducting transition temperature of the bulk was 35 K. After all, such in situ method to fabricate MgB2 showed a great advantage in some aspects, as its low-cost precursors, low sintering temperature, small grain-size and high superconducting transition temperature in the formed MgB2, which have the potential in industrial scale fabrication of MgB2 bulks and wires.

A Novel Gas–solid Reaction Process to Synthesize Low Oxygen MgB2 Powder Using Mg Vapour

Mg Gas Infiltration for the Fabrication of MgB2 Pellets Using Nanosized and Microsized B Powders

Systematic Investigation into the Effect of Boron Powder Purified by Different Methods on the Microstructures and Superconductivity of MgB2 Bulks

A novel process to produce amorphous nano-sized B useful for MgB2 phase synthesis

A Novel Sintering Protocol to Enhance the Connectivity of Exsitu MgB2 Bulks in an Open System by Using Mg Vapor

Exploration of the Effect of Oxygen on Superconductivity in MgB2 Bulk by Using Boron Powder with Different Particle and Purification

Synthesis of Ultrafine Superconducting Mgb2 by A Convenient Solid-State Reaction Route

In Situ Resistance Analysis of MgB2 Formation Process from Mg(BH4)2

Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder

Influence of Mg and B Stoichiometry on the Formation Behavior of MgB2 Phase

Infiltration Effect of Mg with Different Matter States in the Reaction of MgB2 Bulks

Influence of Raw Mg Powder Shape on Behavior of Phase Formation for Mg-B System

Low-temperature synthesis of superconducting nanocrystalline MgB2

Infiltration effect of Mg with different matter states in the reaction of MgB 2 bulks

Effect of nanometer-sized B powder on phase formation of polycrystalline MgB2

Low-temperature Sintering to Fabricate MgB2 by Using Mg(BH4)2 As Precursor

Thermochemistry of MgB2 Thin Film Synthesis

High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor

The mechanism of pore formation in superconducting MgB2 synthesized at low temperature by in-situ process

Experimental Study on Phase Transformation Between Mgb2 and Mgb4

Preparation and Characterization of Mg-Al-B Alloy (Mg0.5Al0.5B2) Via High-Temperature Sintering