The Size Effect of Raw Materials on the Phase Formation of Polycrystalline Mgb2

Chenggang Zhuang,Xiaoxian Liu,Tao Guo,Bo Wang,Xingguo Li,Chinping Chen,Qingrong Feng

DOI: https://doi.org/10.1088/0953-2048/20/12/007

2007-01-01

Abstract:The effect of the size of the B powder and the Mg powder on MgB2 phase formation has been studied by the technique of in situ high-temperature resistivity (HT-rho(T)) measurement. Two characteristic temperatures indicating the phase formation, the onset point, T-onset, and the completion point, T-PF, were directly determined during the continuous heating process. These two temperatures of the samples synthesized using nanometer-size B powder (Nano-B) and micrometer-size B powder (Micro-B) with nanometer-size Mg (Nano-Mg) are almost the same, i.e. T-onset = 713 K and TPF similar to 763 K, respectively, indicating that the phase formation temperature of MgB2 does not primarily depend on the particle size of the B powder. A similar process was then carried out on Mg powders with the same B powder. An exponential relationship between the onset phase formation temperature and the Mg powder size is clearly shown, which can be fully fitted by a modulated diffusion equation and which gives Q = 421 kJ mol(-1) describing the grain boundary activation energy of Mg diffusing into B. We also find that the MgB2 crystallites along the [101] direction have the lowest formation energy, revealed by x-ray diffraction (XRD) analysis on raw Mg powders, and the corresponding MgB2 crystallites aligned along [101] will be formed preferentially in the sintering process. This result is useful for the understanding of MgB2 phase formation in the solid reaction process.