High-flux dual-phase percolation membrane for oxygen separation
Shu Wang,Lei Shi,Zhiang Xie,Yuan He,Dong Yan,Man-Rong Li,Juergen Caro,Huixia Luo
DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.06.039
IF: 5.7
2019-12-01
Journal of the European Ceramic Society
Abstract:<p>A series of composites based on (100-<em><sub>x</sub></em>)wt.%Ce<sub>0.9</sub>Pr<sub>0.1</sub>O<sub>2-</sub>δ-<em>x</em>wt.%Pr<sub>0.6</sub>Ca<sub>0.4</sub>FeO<sub>3-</sub>δ (<em>x</em> = 25, 40 and 50) doped with the cheap and abundant alkaline earth metal Ca<sup>2+</sup> at the A-site has been successfully designed and fabricated. The crystal structure, oxygen permeability, phase and CO2 stability were evaluated. The composition of 60wt.%Ce<sub>0.9</sub>Pr<sub>0.1</sub>O<sub>2-</sub>δ-40wt.%Pr<sub>0.6</sub>Ca<sub>0.4</sub>FeO<sub>3-</sub>δ(60CPO-40PCFO) possesses the highest oxygen permeability among three studied composites. At 1000 °C, the oxygen permeation fluxes through the 0.3 mm-thickness 60CPO-40PCFO membranes after porous La<sub>0.6</sub>Sr<sub>0.4</sub>CoO<sub>3-</sub>δ each to 1.00 mL cm<sup>−2</sup> min<sup>−1</sup> and 0.62 mL cm<sup>−2</sup> min<sup>−1</sup> under air/He and air/CO<sub>2</sub> gradients, respectively. <em>In situ</em> XRD results demonstrated that the 60CPO-40PCFO sample displayed a perfect structural stability in air as well as CO<sub>2</sub>-containing atmosphere. Thus, low-cost, Co-free and Sr-free 60CPO-40PCFO has high CO<sub>2</sub> stability and is economical and environmental friendly since the expensive and volatile element Co was replaced by Fe and Sr was waived since it easily forms carbonates.</p>
materials science, ceramics