Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Mechanical Properties of ZrB2–SiC Ceramics Prepared by Polymeric Precursor Route

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

Effect of ZrB2 powders on densification, microstructure, mechanical properties and thermal conductivity of ZrB2-SiC ceramics

SPS densification and ablative performance of ZrB2–SiC–ZrC composites derived from the ternary powders by sol-gel

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Mechanical Properties of ZrB<sub>2</sub>-Based Ceramics Reinforced by Nano-SiC Whiskers

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

SPS Sintering Behavior and Microstructure of ZrB2-SiCpl Composite Ceramics

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

Effects of ZrB2 powders on microstructure and mechanical properties of ZrB2-SiCw ceramics

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Synergistic Toughening Effect of SiC Whiskers and Particles in ZrO2–Al2O3–SiC Ceramics

Synthesis of ZrB2-SiC-ZrC Composite Powders with Core-Shell Structure Via Sol-Gel Molecular Modulation

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

Comparison of ZrB2–SiC Ceramics with Yb2O3 Additive Prepared by Hot Pressing and Spark Plasma Sintering