Effect of Co Content on the Structure and Magnetic Properties of Melt-Spun Fe55-xCoxPt15B30 Alloys

马殿国,王英敏,李艳辉,张伟
DOI: https://doi.org/10.11900/0412.1961.2016.00485
IF: 1.797
2017-01-01
ACTA METALLURGICA SINICA
Abstract:Fe-Pt-B nanocomposite magnets have attracted much attention because of their excellent hard magnetic properties, in which the face-centered-tetragonal FePt (L1(0)) phase ensures high coercivity (H-i(c)) and the Fe2B phase provides high magnetic saturation. A high H-i(c), however, is hard to reach at low Pt concentrations in these nanocomposite magnets. It is known that a high concentration of B favors the formation of L1(0) phase in Fe-Pt-B alloys with low Pt concentration, but the annealed microstructure is usually coarse-grained due to their low amorphous-forming abilities, and the magnetic properties get deteriorated. Replacement of Fe with Co is expected to enhance the amorphous-forming ability of Fe-Pt-B alloys with low Pt and high B concentrations, and to improve their magnetic properties. In this work, the structure and magnetic properties of as-quenched and annealed Fe55-xCoxPt15B30 (x= 0 similar to 45, atomic fraction, %) alloys have been investigated. Melt-spun ribbons were prepared by melt spinning, followed by vacuum annealing at different temperatures. The structure and magnetic properties of the samples were examined by XRD, TEM and a vibrating sample magnetometer (VSM). The results indicate that single amorphous phase is formed in the alloys at x=15 similar to 45. After appropriate annealing, a nanocomposite structure consisting of L1(0) and (Fe, Co)(2)B phases is obtained at x=0 and 15, and an additional (Fe, Co) B phase gets formed at x=30 and 45. A fine microstructure with mean grain size of similar to 18 nm has been obtained in the annealed alloys with x=15 similar to 45. In these nanocomposite alloys, the best hard magnetic property with an energy product of 94.4 kJ/m(3) is reached at x=15. With increasing Co content, the H-i(c) gradually increases to a maximum value of 413.7 kA/m at x=30, and then decreases at higher Co contents, which are attributed to the change of the magnetocrystalline anisotropy in L1(0) phases with different c/a ratios.
What problem does this paper attempt to address?