Magnetic Coupling in Co1−xPtx (x>0.5) Nanowires Electrodeposited on an AAO Template

W Chen,Z Li,GB Ji,SL Tang,M Lu,YW Du

DOI: https://doi.org/10.1016/j.ssc.2004.11.001

IF: 1.934

2004-01-01

Solid State Communications

Abstract:Thirty nanometer diameter Co–Pt nanowires of different composition were fabricated by electrodepositing the Co and Pt atoms to nanoporous anodized aluminium oxide (AAO) templates. The structure and magnetic properties are studied by transmission electron microscopy (TEM), induction-coupled plasma spectrometer (ICP), X-ray diffraction (XRD) and vibrating sample magnetometer (VSM). The as deposited nanowires with Pt content about 50at.% present a single ferromagnetic phase of fcc CoPt. When the Pt content of the nanowires varies from about 55 to about 75at.%, the nanowires include a soft phase of fcc CoPt3 and a relatively hard phase of fcc CoPt and the two phases are separate as seen from the hysteresis loops. After annealing to 600°C, the two phases coupled completely and the coupled phase has the same coercivity as the original hard one.