Abstract:Toughening with little rigidity loss was achieved by adding high density polyethylene (HDPE) into polypropylene/ethylene-propylene random copolymer (PP/EPR) blends to fabricate a series of PP/EPR/HDPE ternary blends with core–shell dispersed particles. Morphology observations revealed that the addition of HDPE leads to the appearance of core–shell dispersed particles in PP matrix, i.e., HDPE core encapsulated in EPR shell. Dynamic mechanical analysis results showed that the introduction of HDPE could increase glass transition temperature (Tg) and loss factor peak area of EPR in PP/EPR/HDPE blends, which is similar to the effect of adding EPR in PP/EPR. The shrinkage behavior results suggested that the increase of glass transition temperature of EPR was induced by the mismatch of thermal expansion coefficients of components and the larger peak area was ascribed to the stronger relaxation friction of EPR. According to percolation of stress volumes, the interparticle distance was proposed to be a key factor of toughening effect of rubber particles in thermoplastic and thereby a toughening mechanism about the equivalent rubber content was established to explain balanced toughness-strength improvement of PP/EPR/HDPE blends with core–shell particles. The rubber particles with core–shell structure lead to the increase of particle size and the decrease of interparticle distance on the premise of not increasing actual rubber content, resulting in a notable improvement of toughness, while the ‘hard’ core made from HDPE component provides a satisfied rigidity.

High-Density Polyethylene-Based Ternary Blends Toughened by PA6/PBT Core–Shell Particles

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Research on Toughening Modification of Copolymerized Polypropylene Using Polyolefin Elastomers

Fabrication and toughening mechanism of high toughness PP/SEBS/HDPE blends with core‐shell particles

In Situ Formation of the Core–Shell Particles and Their Function in Toughening PA6/SEBS-g-MA/PP Blends

Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

Toughening Effects of "Core-Shell" Particles in PA6/SEBS-g-MA/PPO Blends

Toughening of PBT by POE/POE-g-GMA Elastomer Through Regulating Interfacial Adhesion and Toughening Mechanism

Toughening with Little Rigidity Loss and Mechanism for Modified Polypropylene by Polymer Particles with Core–shell Structure

Effect of Core-Shell Particles Dispersed Morphology on the Toughening Behavior of PBT/PC Blends

Toughening Mechanism of Polypropylene Bends with Polymer Particles in Core-Shell Structure: Equivalent Rubber Content Effect Related to Core-Shell Interfacial Strength

Highly toughened PA6 using residue of plasticized PVB film via two-step reactive melt blending

Modification of the Reactive Core-Shell Particles Properties to Prepare PBT/PC Blends with Higher Toughness and Stiffness

Investigation of toughening mechanism about core-shell morphology in bio-based polyamide ternary composites

Toughening of Polylactide with Epoxy-Functionalized Methyl Methacrylate-Butadiene Copolymer

Preparation and Properties of Poly(Ethylene Terephthalate)/Poly(Butylene Terephthalate) Alloys with High Toughness

Toughened poly(butylene terephthalate) by epoxided ethylene-propylene-diene-rubber

Mechanism and properties of Super-Toughened ternary blends with unique 'Tassel-Bundle' morphology

Toughening of PBT/PC Blends with Core-Shell Modifier

Toughness enhancement of polyamide 6,12 with intermolecular hydrogen bonding with 3‐pentadecylphenol

Stable nanoscale sea-island structure of biobased polyamide 56/poly (butylene adipate- co -terephthalate) blends compatibilized by interfacial hyperbranched structure: Toward biobased polymer blends with ultrahigh toughness