Abstract:β-Ga2O3 nanostructures, including nanowires (NWs), nanosheets (NSHs), and nanorods (NRs), were synthesized using thermally dewetted Au nanoparticles as catalyst in a chemical vapor deposition process. The morphology of the as-grown β-Ga2O3 nanostructures depends strongly on the growth temperature and time. Successful growth of β-Ga2O3 NWs with lengths of 7-25 μm, NSHs, and NRs was achieved. It has been demonstrated that the vapor-liquid-solid mechanism governs the NW growth, and the vapor-solid mechanism occurs in the growth of NSHs and NRs. The X-ray diffraction analysis showed that the as-grown nanostructures were highly pure single-phase β-Ga2O3. The bandgap of the β-Ga2O3 nanostructures was determined to lie in the range of 4.68-4.74 eV. Characteristic Raman peaks were observed with a small blue and red shift, both of 1-3 cm-1, as compared with those from the bulk, indicating the presence of internal strain and defects in the as-grown β-Ga2O3 nanostructures. Strong photoluminescence emission in the UV-blue spectral region was obtained in the β-Ga2O3 nanostructures, regardless of their morphology. The UV (374-377 nm) emission is due to the intrinsic radiative recombination of self-trapped excitons present at the band edge. The strong blue (404-490 nm) emissions, consisting of five bands, are attributed to the presence of the complex defect states in the donor (VO) and acceptor (VGa or VGa-O). These β-Ga2O3 nanostructures are expected to have potential applications in optoelectronic devices such as tunable UV-Vis photodetectors.

Self-consistent Growth of Single-Crystalline (2̄01)Β-Ga2o3nanowires Using a Flexible GaN Seed Nanocrystal

beta-Ga2O3 nanowires: controlled growth, characterization, and deep-ultraviolet photodetection application

From powder to nanowire: A simple and environmentally friendly strategy for optical and electrical GaN nanowire films

Nanowire-Seeded Growth of Single-Crystalline (010) Β-Ga2 O3 Nanosheets with High Field-Effect Electron Mobility and On/Off Current Ratio.

Control of growth orientation of GaN nanowires

A Study On Self-Assembled Gan Nanobelts By A New Method: Structure, Morphology, Composition, And Luminescence

Growth of Zinc Blende Gaas/Algaas Radial Heterostructure Nanowires by A Two-Temperature Process

A simple method for the growth of high-quality GaN nanobelts

Simple And High-Yield Method For Synthesizing Single-Crystal Gan Nanowires

-growth orientation dependence of Ga2O3 nanowires on Cu3As seeds via vapor-solid-solid mechanism

Ga2O3 nanowires grown on GaN–Ga2O3 core–shell nanoparticles using a new method: Structure, morphology, and composition

Two-step synthesis of one-dimensional single crystalline GaN nanowires

β-Ga2O3 Nanostructures: Chemical Vapor Deposition Growth Using Thermally Dewetted Au Nanoparticles as Catalyst and Characterization

Defect-pit-assisted Growth of GaN Nanostructures: Nanowires, Nanorods and Nanobelts

Fabrication and Characterization of Β-Ga2o3 Optical Nanowires

Controllable Ga/Ga 2 O 3 Nanowire Growth at High Temperatures Enabled by Au and Pd Quantum Dot Catalysts

Catalyst-free Synthesis of Well-Aligned ZnO Nanowires on In0.2Ga0.8N, GaN, and Al0.25Ga0.75N Substrates.

Controllable Growth of Gallium Oxide Nanowires by Chemical Vapor Deposition

The growth of ultralong and highly blue luminescent gallium oxide nanowires and nanobelts, and direct horizontal nanowire growth on substrates

Gallium nitride nanowires grown by hydride vapor phase epitaxy

Synthesis of Single Crystalline GaN Nanoribbons on Sapphire (0001) Substrates