Abstract:External gelation process was used to prepare ceria-stabilized zirconia (CSZ) microspheres at various conditions. The effects of nozzle inner diameter, broth flow rate and Zr concentration on microsphere diameter, standard deviation (SD) of diameter and sphericity were investigated. The microsphere diameter decreased, while sphericity increased as flow rate increased. Diameter SD was low at the middle flow rate range. Diameter and sphericity increased as Zr concentration increased. Crushing strength and density increased steadily while cracking rate decreased to 0 by 0.84 mol/L. The quantified results were summarized as boundary conditions for preparation of CSZ microspheres. They were depicted into a size control diagram. The CSZ microspheres from 96 to 573 μm in size could be prepared by selecting preparation conditions according to the diagram. The effectiveness of size control was confirmed by verification experiments. The obtained CSZ microspheres were characterized by optical microscopy, scanning electron microscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM). Microscopic images showed their monodispersity, good sphericity and smooth surface. XRD and TEM results revealed their well-crystallized CSZ phase.

Precisely Controlling Preparation of Ceria‐Stabilized Zirconia Microspheres of ~100 Μm by External Gelation

Preparation of Ceria-Stabilized Zirconia Microspheres by External Gelation: Size Control

Preparation of Small Size Ceria Stabilized Zirconia Microspheres by External Gelation: Effect of Vibration Frequency

A Comparative Study of Small-Size Ceria–zirconia Microspheres Fabricated by External and Internal Gelation

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of Monodisperse ZrO2 Ceramic Microspheres (>200 Μm) by Co-Axial Capillary Microfluidic Device Assisted Internal Gelation Process

Preparation of Small-Sized ZrO<sub>2</sub> Microspheres by Capillary Microfluidic Device Assisted Internal Gelation Process

Preparation Of Small-Sized Zro2 Microspheres By Capillary Microfluidic Device Assisted Internal Gelation Process

An Improved Internal Gelation Process for Preparing Zro2 Ceramic Microspheres Without Cooling the Precursor Solution

An improvement of microfluidic‐assisted internal gelation in the preparation of millimeter‐sized ceramic microspheres

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

Preparation of Monodisperse YSZ Ceramic Microspheres by High-Throughput and Instant-Mixing Droplet Microfluidic System

Microfluidic Fabrication of ZrO2 Microspheres Using Improved External Gelation Aided by Polyacrylamide Networks

Microfluidic Fabrication of Ceramic Microspheres with Controlled Morphologies

Preparation of ZrO2 microspheres by spray granulation

Gel-casting Preparation of Ceramic ZrO2 Composition Microspheres

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

Preparation of Ultrafine Zirconia Suspension for Gelcasting

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Fabrication of ceramic microspheres by diffusion-induced sol-gel reaction in double emulsions.