Abstract:Hypothesis: Zirconia microparticles produced by sol-gel synthesis have great potential for photonic applications. To this end, identifying synthetic methods that yield reproducible control over size uniformity is important. Phase transformations during thermal cycling can disintegrate the particles. Therefore, understanding the parameters driving these transformations is essential for enabling high-temperature applications. Particle morphology is expected to influence particle processability and stability. Yttria-doping should improve the thermal stability of the particles, as it does in bulk zirconia. Experiments: Zirconia and YSZ particles were synthesized by improved sol-gel approaches using fatty acid stabilizers. The particles were heated to 1500 °C, and structural and morphological changes were monitored by SEM, ex situ XRD and high-energy in situ XRD. Findings: Zirconia particles (0.4-4.3 μm in diameter, 5-10% standard deviation) synthesized according to the modified sol-gel approaches yielded significantly improved monodispersities. As-synthesized amorphous particles transformed to the tetragonal phase at ∼450 °C with a volume decrease of up to ∼75% and then to monoclinic after heating from ∼650 to 850 °C. Submicron particles disintegrated at ∼850 °C and microparticles at ∼1200 °C due to grain growth. In situ XRD revealed that the transition from the amorphous to tetragonal phase was accompanied by relief in microstrain and the transition from tetragonal to monoclinic was correlated with the tetragonal grain size. Early crystallization and smaller initial grain sizes, which depend on the precursors used for particle synthesis, coincided with higher stability. Yttria-doping reduced grain growth, stabilized the tetragonal phase, and significantly improved the thermal stability of the particles.

Preparation of Small Size Ceria Stabilized Zirconia Microspheres by External Gelation: Effect of Vibration Frequency

Precisely Controlling Preparation of Ceria‐Stabilized Zirconia Microspheres of ~100 Μm by External Gelation

Preparation of Ceria-Stabilized Zirconia Microspheres by External Gelation: Size Control

A Comparative Study of Small-Size Ceria–zirconia Microspheres Fabricated by External and Internal Gelation

Preparation of Small-Sized ZrO<sub>2</sub> Microspheres by Capillary Microfluidic Device Assisted Internal Gelation Process

Preparation Of Small-Sized Zro2 Microspheres By Capillary Microfluidic Device Assisted Internal Gelation Process

Preparation of Monodisperse ZrO2 Ceramic Microspheres (>200 Μm) by Co-Axial Capillary Microfluidic Device Assisted Internal Gelation Process

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

Gel-casting Preparation of Ceramic ZrO2 Composition Microspheres

An improvement of microfluidic‐assisted internal gelation in the preparation of millimeter‐sized ceramic microspheres

Microfluidic Fabrication of Ceramic Microspheres with Controlled Morphologies

An Improved Internal Gelation Process for Preparing Zro2 Ceramic Microspheres Without Cooling the Precursor Solution

The Fabrication of ZrO2–ZrC Microspheres by Internal Gelation and Carbothermal Reduction Process

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Preparation of Nanopowders ZrO2 by Ultrasound Enhanced Sol-Gel Reaction

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Preparation of Ultrafine Zirconia Suspension for Gelcasting

Synthesis and thermal stability of zirconia and yttria-stabilized zirconia microspheres

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Effect of Al2O3on the Process Performance of ZrO2Microspheres

Synthesis of yttria-stabilized zirconia powders for plasma spray by internal gelation