Abstract:The aim of this study is to analyze the ballistic impact behavior of a panel made of Twaron CT736 fabric with a 9 mm Full Metal Jacket (FMJ) projectile. Three shots are fired at different velocities at this panel. The ballistic impact test procedure was carried out in accordance with NIJ 010106. The NIJ-010106 standard is a document that specifies the minimum performance requirements that protection systems must meet to ensure performance. The 9 mm FMJ projectile is, according to NIJ 010106, in threat level II, but the impact velocity is in threat level IIIA. Analysis of macro-photographs of the impact of the Twaron CT736 laminated fabric panel with a 9 mm FMJ projectile involves a detailed examination of the images to gather information about the material performance and failure mechanisms at the macro- or even meso-level (fabric/layer, thread). In this paper, we analyze numerically and experimentally a panel consisting of 32 layers, made of a single material, on impact with a 9 mm FMJ projectile. The experimental results show that following impact of the panel with three projectiles, with velocities between 414 m/s and 428 m/s, partial penetration occurs, with a different number of layers destroyed, i.e., 15 layers in the case of the projectile velocity of 414 m/s, 20 layers of material in the case of the panel velocity of 422 m/s and 22 layers destroyed in the case of the projectile velocity of 428 m/s. Validation of the simulated model is achieved by two important criteria: the number of broken layers and the qualitative appearance. Four numerical models were simulated, of which three models validated the impact results of the three projectiles that impacted the panel. Partial penetration occurs in all four models, breaking the panel in the impact area, with only one exception, i.e., the number of layers destroyed, in which case the simulation did not validate the validation criterion. The performance of Twaron CT736 fabric is also given by the indentation depth values by two methods: according to NIJ 0101.06 and by 3D scanning. The NIJ 010106 standard specifies that a panel provides protection when the indentation depth values are less than 0.44 mm.

Dynamic Response of Kevlar®29/epoxy Laminates under Projectile Impact-Experimental Investigation

Impact response and damage evolution of triaxial braided carbon/epoxy composites. Part I: Ballistic impact testing

Experimental and numerical analysis of ballistic impat and material characterization of GFRP and Kevlar 29/epoxy composite laminate

Experimental and numerical investigations on the dynamic response of woven carbon fiber reinforced thick composite laminates under low-velocity impact

Dynamic fracture in CFRP laminates: Effect of projectile mass and dimension

Experimental Estimation of Energy Absorbed and Impact Strength of Kevlar/Basalt-Epoxy Interwoven Composite Laminate Added with Al2O3 Nanoparticles after High-Velocity Bullet Impact

Dynamic response and failure of CFRP Kagome lattice core sandwich panels subjected to low-velocity impact

Thickness effect on ballistic impact behavior of hybrid carbon/Kevlar composites

High‐velocity impact resistance and energy absorption behavior of Carbon‐Kevlar hybrid composite laminates

Ballistic impact experiments of titanium-based carbon-fibre/epoxy laminates

Effects on Ply Orientation of Kevlar/Epoxy for Ballistic Impact in Bulletproof Vest Using Non-linear Finite Element Analysis

Impact response of thermoplastic composites – Experiments and modeling

Dynamic Failure Mechanisms in Woven Ceramic Fabric Reinforced Metal Matrix Composites During Ballistic Impact

Effect of fiber architecture on the impact resistance of composite panels subjected to metallic projectile

Low-Velocity Impact and Post-Impact Residual Flexural Properties of Kevlar/EP Three-Dimensional Angle-Interlock Composites

Experimental and Simulation Study on Failure of Thermoplastic Carbon Fiber Composite Laminates under Low-Velocity Impact

Statistical Mechanics of Kevlar® KM2® Plus Nanostructure: Deformations and High-Rate Impact

Soft impact of GLARE fiber metal laminates

FEA of Plain Woven Kevlar/Epoxy Composites Subjected to Normal and Oblique Impact with Multi-Scale Modelling

Experimental and Numerical Analysis of the Damage Mechanism of an Aramid Fabric Panel Engaged in a Medium-Velocity Impact

An experimental study of the dynamic responses of carbon fiber reinforced polymer composite laminates subjected to ice impact