Abstract:Combined experimental and simulation analysis of bending failure of GLARE laminates. GLARE laminate experiences multiple damage modes during bending failure, including fiber fracture, matrix cracking, interlayer delamination, and fracture of aluminum alloy. In most cases, two or more failure modes occur together, which makes the damage process complex and unpredictable. This paper proposes a combination of experimental testing and numerical simulation to investigate the influence of fiber lay‐up direction and center open‐hole on the bending failure behavior of GLARE laminate. Simultaneously, Acoustic Emission (AE) technology was used to monitor the bending process of GLARE laminates in real‐time, and a numerical simulation model for the three‐point bending of GLARE laminates was established. The experimental results showed that the bending strength of intact specimens decreased significantly with the increase of the fiber off‐axis angle, whereas the strength retention of open‐hole specimens increased significantly with the increase of the fiber off‐axis angle. Based on the K‐means++ clustering algorithm, the peak frequencies corresponding to different damage modes of GLARE laminates were identified as follows: aluminum alloy damage [1–70 kHz], matrix cracking [93–210 kHz], interlaminar delamination [211–304 kHz], and fiber breakage [304–516 kHz]. The simulation results agreed well with the experimental results, showing that the damage in intact specimens initiated at the laminate edges and propagated sequentially along the thickness direction, while the damage in open‐hole specimens initiated at the hole edges and then propagated towards the laminate edges. Highlights The present study investigated the effects of fiber lay‐up direction and central open‐hole on the bending performance and failure behavior of GLARE laminate. In‐situ monitoring of the GLARE laminate during three‐point bending was conducted using AE technology. A model for simulating the progressive damage of GLARE laminate was established and its accuracy was verified.

Soft impact of GLARE fiber metal laminates

Micro Failure Analysis of Fiber Metal Laminates

Low velocity impact response of fiber metal laminates with nano-patterned metal surfaces

Soft Impact Response of Laminated Glass Plates

Study of Low-Velocity Impact Behavior of Hybrid Fiber-Reinforced Metal Laminates

Dynamic impact behavior and notched fatigue life of GLARE laminates

Energy dissipation mechanism of fiber metal laminate under low-velocity impact

Identifying the contributions of constituents to the fracture performance and failure mechanism of fiber metal laminate

Simulation on Impact Response of FMLs: Effect of Fiber Stacking Sequence, Thickness, and Incident Angle

Numerical and experimental investigation on the oblique successive impact behavior and accumulated damage characteristics of fiber metal laminates

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact

Effect of boundary conditions on the low‐velocity impact damage mechanism of fiber metal laminate

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Notched behavior of hybrid glass/aluminum/titanium fiber metal laminates

Effect of symmetric and asymmetric aluminum arrangements on the low‐velocity impact performance of glass fiber‐reinforced aluminum laminate (GLARE)

Experimental and numerical studies of the simultaneous effects of temperature and impact velocity on ballistic behavior of GLARE

Study of the dynamic response and damage evolution of carbon fiber/ultra-thin stainless-steel strip fiber metal laminates under low-velocity impact

On impact behavior of fiber metal laminate (FML) structures: A state-of-the-art review

Residual tension behavior and damage evolution mechanisms of fiber metal laminates with various low-velocity impacted damage

Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM

GLARE deformation in low-restraint state: Tensile and bending behavior