Abstract:Abstract GLARE laminates have emerged as a favored option for the construction of fuselage and wing skins in large airliners, owing to their exceptional mechanical characteristics. Nevertheless, the incorporation of open‐hole designs poses a challenge as it disrupts the continuity of the laminates, resulting in stress concentration and subsequent damage. To investigate the impact of various layup orientations and hole sizes on the tensile properties of open‐hole GLARE laminates, this study conducted axial tensile tests. Additionally, the tensile damage process was monitored using DIC and AE techniques, enabling the identification of damage patterns and the analysis of their evolution. The results demonstrate a noteworthy decline in the ultimate strength and failure strain as the size of the opening increases. Moreover, the retention rate of failure strain displays a marked sensitivity to the layup orientation. In conjunction with observations made through DIC and SEM, the k‐means++ algorithm successfully clustered peak frequencies, thereby revealing distinct damage patterns and their corresponding frequency ranges as aluminum alloy damage [0–90 kHz], matrix cracking [104–174 kHz], fiber/matrix debonding [175–224 kHz], interlaminar delamination [234–300 kHz], and fiber fracture [304–469 kHz]. AE cumulative counts were utilized to evaluate the progression of individual damage modes. The results emphasize that matrix cracking demonstrates the most substantial cumulative counts, whereas damage to the fibers and aluminum alloy noticeably affects the load‐carrying capability of the laminate. Furthermore, the fibers/matrix debonding and interlaminar delamination, exhibit heightened susceptibility to layup orientation and hole size. Highlights The tensile performance evaluation of GLARE laminates with open‐hole varying layup orientations and hole sizes was investigated. A combination of DIC and AE techniques was used to monitor the tensile damage process. Damage pattern was identified based on the observations of DIC and SEM. An approach based on Pearson's correlation coefficient and k‐means++ clustering algorithm was used for damage pattern recognition in GLARE laminates. AE cumulative counts were employed to assess the evolution of each damage mode.

Notched behavior of hybrid glass/aluminum/titanium fiber metal laminates

Local Reinforcement in Notched Fiber Metal Laminates by Bonding Titanium Patch

Low velocity impact response of fiber metal laminates with nano-patterned metal surfaces

Identifying the contributions of constituents to the fracture performance and failure mechanism of fiber metal laminate

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Delamination Behavior of an Advanced Al-Li Alloy Laminate During Fatigue Crack Growth

GLARE deformation in low-restraint state: Tensile and bending behavior

Soft impact of GLARE fiber metal laminates

Experimental and theoretical study on residual ultimate strength after impact of CF/PEEK-titanium hybrid laminates with nano-interfacial enhancement

Mechanical properties and formability behavior of glass-reinforced aluminum laminate, developed by semi-cured process

A Novel Dual-Stage Failure Criterion Based on Forming Limit Curve for Uncured GLARE

Quasi‐static fracture characterization of fiber metal laminate with crack resistance curve based on δ5

Open-hole Tensile Progressive Damage and Failure Prediction of Carbon Fiber-Reinforced PEEK–titanium Laminates

Dynamic impact behavior and notched fatigue life of GLARE laminates

Study of Low-Velocity Impact Behavior of Hybrid Fiber-Reinforced Metal Laminates

Investigation into the Fiber Orientation Effect on the Formability of GLARE Materials in the Stamp Forming Process

Tensile and flexural mechanical attributes of hybrid carbon/basalt fiber metal laminates under various hybridization and stacking sequences

Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM

Assessment of tensile damage mechanism of open‐hole GLARE laminates based on acoustic emission and digital image correlation techniques

Comparative Study on the Influence of Hybrid Nano Fillers Modified Epoxy in the Mechanical Behavior of GLARE Laminates

A novel active hydroforming & curing process to manufacture GLARE laminates: Numerical and experimental investigations