Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Oxidation Behavior of C/SiC-Ti3SiC2 at 800–1300 °C in Air

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

High Temperature Oxidation Behavior of SiC Coating Materials

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100°C

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

High Temperature Oxidation Resistance Of Ti3sic2 In Air And Low Oxygen Atmosphere

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Oxidation Behavior of TiC-containing Ti3AlC2based Material at 500–900 °C in Air

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Effect of Oxidation Time on Fracture Behavior of C/SiC Composites at 800 °C in Air

High temperature oxidation behavior of reaction-bonded silicon carbide

Study on the oxidation mechanism of Al-SiC composite at elevated temperature

Oxidation behavior of 3D Hi–Nicalon/SiC composite

Oxidation Behaviour of C–SiC–ZrC Composite

The anti‐oxidation behavior of the Ti3SiC2/Cu composites at high temperatures

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air