Abstract:Nickel-based alloys are being considered as construction materials for various components in high-efficiency steam turbines with envisaged operating temperatures around 700 °C. In the present study, the steam oxidation behaviour of the nickel-based alloy 625 in the temperature range of 700–800 °C was investigated whereby exposures up to 10000 h were carried out. Gravimetric data in combination with results from a variety of post exposure analysis techniques showed in all cases the formation of protective oxide scales mainly consisting of chromia with minor amounts of outer Cr/Mn spinel and internal silica. The phases found in the bulk alloy after long-term exposure were mainly needle-shaped δ-Ni3(Nb,Mo) phase, μ-phase and Si-rich η-M6C carbide. Microstructural features and phase formation were found to be related to minor variations in the alloy composition, especially iron and silicon content. The oxidation-induced chromium depletion caused a number of microstructural changes in the subsurface depletion layer. Most important was an enrichment of the intermetallic δ-phase at the scale–alloy interface. DICTRA modelling revealed this effect to be caused by uphill diffusion as a result of a negative niobium activity gradient in the subscale chromium depletion zone. Although the available kinetic and thermodynamic data allowed qualitative explanation of the δ-phase enrichment, the databases do not correctly describe the high molybdenum solubility in the δ-phase.

Steam Oxidation Behavior of Alloy 617 at 900 °C to 1100 °C

High-Temperature Air and Steam Oxidation and Oxide Layer Characteristics of Alloy 617

Characterization of Oxide Scales on Super-Alloy HR120 at 1000 °C in Air and Steam Environments

Oxidation behaviour and microstructural stability of alloy 625 during long-term exposure in steam

Oxidation Behavior of a New Fe–Ni–Cr-based Alloy in Pure Steam at 750 °C

High Temperature Oxidation of Alloy 617, 740, HR6W and Sanicro 25 in Supercritical Water at 650°C

Precipitation behavior of oxide dispersion strengthened Alloy 617

High Temperature Oxidation of Newly Developed Alloy 282 in the Flowing-Air and Steam Condition at 900–1100 °C

Effect of Minor Alloying Elements on the Oxidation Behavior of Ni-Base Alloys in a High-Temperature Steam Environment

High Temperature Oxidation of Superalloys in Steam Environment

Field Studies of Steam Oxidation Behavior of Austenitic Heat-Resistant Steel 10Cr18ni9cu3nbn

Short-time Oxidation of Alloy 690 in High-temperature and High-pressure Steam and Water

Effect Of Steam Temperature On Oxidation Behavior Of Gh2984 Alloy As A Candidate For 700 Degrees C Advanced Ultra-Supercritical Boilers

Characteristics of Oxidation and Oxygen Penetration of Alloy 690 in 600 °C Aerated Supercritical Water

The oxidation behavior of nickel‐based alloy Inconel 617 in supercritical water

Steam Oxidation of Austenitic Heat-Resistant Steels TP347H and TP347HFG at 650–800 °C

Corrosion Performance of Heat-Resisting Steels and Alloys in Supercritical Carbon Dioxide at 650 °C and 15 MPa

High temperature oxidation of CrAl-coated Zr–1 Nb alloy in 1000 – 1300 °C steam

Microstructure understanding of high Cr-Ni austenitic steel corrosion in high-temperature steam

High-temperature steam oxidation behavior and failure mechanisms of Al alloyed Cr coatings on Zr-4 alloy

Oxidation Behavior of Tribaloy T-800 Alloy at 800 and 1,000 °C