Abstract:Nickel based superalloys are widely used in such applications as gas turbine blades due to their excellent mechanical properties at elevated temperatures. Oxidation is one of the life limiting factors at such temperatures since it accelerates failure mechanisms, e.g. fatigue and creep. In this project, oxidation behavior of Ni-3Al-4.8Ti-9.5Co-14Cr (wt.%) superalloy was investigated under various testing conditions. The alloy was investment-cast with preferential crystal growth direction [100]. Isothermal oxidation tests were carried out at 800°C for 150h. Cyclic oxidation tests were then conducted between 100-800°C for 150 one-hour cycles. An additional one-hour cycle was tested to replicate real-life working condition of the alloy, which consisted of heating the samples up to 800°C followed by slow cooling to 400°C. During the testing, samples were periodically taken from the furnace and weighted with an accuracy of 10 -4 g to calculate the weight gain and to analyze the microstructure of formed oxide. Scanning electron microscopy (SEM) combined with energy-dispersive spectroscopy (EDS) and X-ray diffraction were used to study the microstructure of oxidation products. The results reveal that the highest amount of weight gain is obtained in isothermal testing, while the lowest in cyclic. Diffusion of Ti and Ni to the free surface results in the early-stage formation of needle-shaped oxide phases followed by severe oxidation of Cr and Al. The layer of chromium oxide is continuous while aluminum oxide is blocky at the deepest position from the free surface. Cracks form at the interface of carbide particles and gamma phase near the free surface of cyclic oxidation samples due to concentration gradient of Ni and Al. Precipitate-free zone are observed near the free surface of all the samples at the end of the tests, but internal oxidation does not occur significantly in all the samples. It is found that temperature fluctuation increases oxide spallation, which causes crack formation. At the same time, in isothermal testing, dense, crack-free layer of oxide form on the surface of superalloy.

Oxidation behaviour and microstructural stability of alloy 625 during long-term exposure in steam

Oxidation Behavior of a New Fe–Ni–Cr-based Alloy in Pure Steam at 750 °C

High-Temperature Air and Steam Oxidation and Oxide Layer Characteristics of Alloy 617

Microstructure understanding of high Cr-Ni austenitic steel corrosion in high-temperature steam

Compatibility of Different Commercial Alloys in High-Temperature, Supercritical Carbon Dioxide

Isothermal short‐term oxidation behavior of MAR‐M246 nickel‐based superalloy at 800°C and 1000°C

Influence of Single- and Double-Aging Treatments on the Mechanical and Corrosion Resistance of Alloy 625

Oxidation Behaviour of New Nickel-Base Superalloys with Varying Aluminium: Niobium Ratio

Modelling compositional changes in nickel base alloy 602 CA during high temperature oxidation

High Temperature Oxidation Behavior of Ni-based High Entropy Superalloys

Chromium Depletion in a Ni-30Cr Alloy During High-Temperature Oxidation

Oxidation behavior of 4774DD1 Ni-based single-crystal superalloy at 980 °C in air

Microstructural changes in alloy 625 during high temperature creep

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

Mechanical Properties and Microstructural Characterization of Aged Nickel-based Alloy 625 Weld Metal

Oxidation of Thin Nickel-Based Superalloy Specimens: Kinetics Study and Mechanical Integrity

Cyclic and Isothermal Oxidation Behavior of a Directionally Solidified Ni-Al-Ti-Co-Cr Superalloy

Influence of composition and heating schedules on compatibility of FeCrAl alloys with high-temperature steam

The Process of Steam Oxidation Degradation of High Cr Steel after 125 000 Hours at 568 °C under 16.5 MPa

Corrosion Behaviour of Ni-based Alloys 230, 617, and 601 in CO2 Gas at 750 and 850°C

Microstructural homogenization and high-temperature cyclic oxidation behavior of a Ni-based superalloy with high-Cr content