Effect Of Steam Temperature On Oxidation Behavior Of Gh2984 Alloy As A Candidate For 700 Degrees C Advanced Ultra-Supercritical Boilers

Yang Zhen,Lu Jin-Tao,Zhang Xia-Ni,Zhao Xin-Bao,Yuan Yong,Dang Ying-Ying,Yin Hong-Fei,Gu Yue-Feng
DOI: https://doi.org/10.11868/j.issn.1001-4381.2015.000305
2018-01-01
Journal of Materials Engineering
Abstract:The oxidation behavior of GH2984 alloy in pure steam at 750*degrees C and 850 degrees C was investigated by using X-ray diffractometer (XRD) and scanning electron microscope equipped with energy dispersive spectra (SEM/EDS). Results show that GH2984 alloy is oxidized parabolically with time. The temperature rising greatly promotes the external and internal oxidation and also the evaporation of Cr. The composition and microstructure of the oxide films change obviously. At 750 degrees C, a compact and sin g le-layered (Cr,Mn)(2)O-3 film is formed on alloy surface ; the number of voids in oxide scale increases at 850 degrees C, whereas a three-layered oxide scale consisting of thin Fe2TiO5 outer layer and much thicker (Cr, Mn)(2)O-3 middle layer and thinner (Nb,Mo)(2)O-5 inner layer is formed at the elevated temperature. Ti and Al are internally oxidized preferentially along grain boundaries to be TiO2 and Al2O3, respectively ; both the number and the size of the two internal oxides increase with the temperature rising.
What problem does this paper attempt to address?