Effect of Yttrium Additions on the High-Temperature Oxidation Behavior of GH4169 Ni-Based Superalloy

Tiantian Wang,Wei Liu,Shufeng Yang,Jingshe Li,Peng Zhao,Hui Xue

DOI: https://doi.org/10.3390/ma17112733

IF: 3.4

2024-06-05

Materials

Abstract:The effect of the active element yttrium and its content on the oxidation behavior of GH4169 Ni-based superalloy at extreme temperature was studied by isothermal oxidation experiments. The results show that the oxide scale of GH4169 alloy presents a multi-layer structure, in which the continuous and dense Cr2O3 oxide layer is located in the subouter layer (II layer) and the continuous Nb-rich layer is in the subinner layer (III layer). These layers can inhibit the diffusion of oxygen and alloying elements, preventing the further oxidation of the alloy. The appropriate addition of yttrium can promote the selective oxidation of Cr element, reduce the thickness of the oxide scale and the oxidation rate of the alloy, inhibit the formation of voids at the interface of the oxide scale/alloy matrix, improve the resistance of the alloy to spalling as well as the adhesion of the oxide scale, and improve the high-temperature oxidation resistance of the alloy. Of those tested, the alloy containing 0.04 wt.%Y has the lowest oxidation weight gain, the slowest oxidation rate, and less oxide scale spalling. Based on this, the effect of yttrium on the high-temperature oxidation behavior of GH4169 Ni-based superalloy and its mechanism were revealed.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

This paper mainly studies the effect of yttrium (Yttrium) addition on the high-temperature oxidation behavior of GH4169 nickel-based superalloys. GH4169 superalloy is widely used in high-temperature components of aircraft engines due to its high-temperature strength, microstructure stability, and oxidation resistance. The study investigates the effect of different yttrium contents on the oxidation behavior of the alloy at extreme temperatures (1000°C) through isothermal oxidation experiments.

The experimental results show that the appropriate addition of yttrium can promote the selective oxidation of chromium elements, forming a continuous and dense Cr2O3 oxide layer, reducing the oxidation rate, suppressing the formation of cavities at the forefront of oxidation products, and enhancing the adhesion between the oxide layer and the alloy matrix, thereby improving the high-temperature oxidation resistance of the alloy. Specifically, the alloy containing 0.04 wt.% yttrium exhibits the lowest weight gain during oxidation, the slowest oxidation rate, and less delamination of the oxide layer.

The paper also mentions that when the temperature exceeds 900°C, the Cr2O3 oxide layer becomes unstable and easily forms volatile CrO3, causing further oxidation of the alloy. Yttrium has a higher activity than chromium and the formed Y2O3 oxide can act as a heterogeneous nucleation core for Cr2O3, which helps to protect the formation of the oxide layer. Previous studies have also confirmed that yttrium can enhance the adhesion between the oxide layer and the alloy matrix, reducing the tendency of oxide layer delamination.

Through oxidation kinetic analysis, oxide phase analysis, surface and cross-section morphology observation, and element distribution detection, the paper reveals the effect of yttrium on the high-temperature oxidation behavior of GH4169 nickel-based superalloys and its mechanism, providing a reference for improving the high-temperature oxidation resistance of the alloy.