Abstract:Defect-free SLM-IN 738LC superalloy samples were fabricated using selective laser melting (SLM). The as-built samples exhibit a cellular structure with fine carbides, γ′ phases, and high-density dislocations at the cell boundary and nano-size γ′ phases in the interior, resulting in excellent deformation resistance and favorable mechanical properties at room temperature, with a yield strength (YS) of 970 MPa, an ultimate tensile strength (UTS) of 1263 MPa, and an elongation (EL) of 33%. This study investigates the evolution behavior of the γ′ phase at different solid solution treatment (SHT) temperatures and its impact on alloy strength and toughness. The 1020 + AHT sample exhibits a uniform distribution of coarse γ′ phases. The samples subjected to 1070 + AHT and 1120 + AHT display a bimodal distribution of γ′ phases. When the SHT temperature was further increased, fine spherical γ′ phases are evenly distributed in the 1160 + AHT and 1200 + AHT samples. Moreover, the γ/γ′ eutectics at the grain boundaries gradually dissolve with increasing SHT temperature, whereas the size and fraction of carbides increase. The room temperature tensile test of the 1070 + AHT sample demonstrated a favorable balance between strength and plasticity (YS = 1217 MPa, UTS = 1472 MPa, EL = 9.25%). This is attributed to the synergistic strengthening effect of the bimodal distribution of the γ′ phase. The temperature-dependent deformation behavior of the 1070 + AHT sample was analyzed at 23 °C, 800 °C, 900 °C, and 1000 °C. At 23 °C, numerous dislocations accumulated around the γ/γ′ interfaces. When the temperature increased to 800–900 °C, the dislocations shearing γ′ phases is activated and the alloy remained high strength. At 1000 °C, both the dislocation shearing and dislocation bypassing mechanisms coexist, resulting in a decrease in the strength of the alloy and an increase in its plasticity. This work provides scientific and theoretical support for SLM-IN 738LC parts with favorable properties.

Effect of yttrium addition on microstructural evolution and high temperature mechanical properties of Ni-based superalloy produced by selective laser melting

Yttrium Induced Formation of New Pores in an As-Cast Nickel-Based Single Crystal Superalloy

Effect of alloying on the microstructure, phase stability, hardness and partitioning behavior of a new dual-superlattice nickel-based superalloy

Effect of Yttrium Addition on Microstructure and Mechanical Properties of Sr-Modified Low-Si Cast Aluminum Alloy

Effect of Y on the Oxidation Behavior of a Directionally Solidified Ni-based Single Crystal Superalloy

Effects of yttrium content on solidification, microstructure, and mechanical properties of laser powder bed fused IN718 superalloy

Nano-crystallization and Mechanical Properties of Y Addition Ti40Zr25Cu9Ni8Be18 Amorphous Alloy

Effects of Yttrium on Microstructure and Mechanical Properties of Mg-6Al Magnesium Alloy

Anisotropy in microstructure and mechanical properties of additively manufactured Ni-based GH4099 alloy

Effect of Yttrium on Microstructures and Properties at Elevated Temperature of Mg-0.8Zr-0.35Zn Alloys

Microstructural evolution and mechanical property of Al–Zr and Al–Zr–Y alloys

Crack Inhibition and Performance Modification of NiCoCr-Based Superalloy with Y2O3 Nanoparticles by Laser Metal Deposition

Microalloying effects of Y on performance of cast nickel-based superalloy IN713C

Effects of yttrium additions on microstructures and mechanical properties of cast Al-Cu-Mg-Ag alloys

Strengthening Effects and Thermal Stability of the Ultrafine Grained Microstructure of a Nickel Base Superalloy at Room and Elevated Temperatures

Effects of Y on Microstructure and Properties of Al-10Mg Alloy

Microstructural Evolution and High-Temperature Strengthening Mechanisms of the in 738LC Superalloy Prepared by Selective Laser Melting

Effect of Yttrium Addition on Microstructures and Room Temperature Tensile Properties of Ti-47 Al Alloy

Significant Enhancement in High-Temperature Tensile Strength of Trace Nano-Y2o3-reinforced TiAl Alloy Prepared by Selective Electron Beam Melting

Effect of yttrium on phase composition and microstructure of FeCoNiAlCrB high entropy alloys

Effect of Y2O3 addition on microstructure and properties of Ti6Al4V by laser melting deposition