The Formation, Evolution and Influence of Gd-Containing Phases in the (gd+b4c)/6061al Composites During Hot Rolling

Z. G. Xu,L. T. Jiang,Q. Zhang,J. Qiao,L. C. Zhang,P. He,J. Ma,G. H. Wu
DOI: https://doi.org/10.1016/j.jallcom.2018.10.212
IF: 6.2
2018-01-01
Journal of Alloys and Compounds
Abstract:A novel boron carbide and gadolinium particles reinforced Al neutron shielding composite (1% Gd+15% B4C)/6061Al was successfully fabricated by vacuum hot pressing method, and its microstructure and tensile properties during hot rolling were studied. The results indicated that, the main Gd-containing phase during hot rolling was Al5Gd3O12, and the size decreased with the increase of the derformation amount. The results of thermodynamic calculations confirmed the possibility of the formation of Gd-containing phases in the preparation process. The main defects of the Gd-containing phases were stacking faults. During the hot rolling process, the mechanical properties of the (1% Gd+15% B4C)/6061Al composite were better than the 15% B4C/6061Al composite. The increase in strength came from the strengthening effect of the Gd-containing phases, which was consistent with the theoretical calculations. Stacking faults in the Gd-containing phases allowed dislocations to slip through, thereby improving the plasticity of the composite.
What problem does this paper attempt to address?