Abstract:B4C ceramics were strengthened by introducing the hard second–phase particles TiB2 and SiC, and the effects of TiB2 and SiC contents on the microstructure and properties of the composites were investigated. B4C–TiB2 binary composites with TiB2 contents of 10, 20, 30, and 40 vol% were prepared by hot pressing. The microstructure, mechanical properties, and electrical properties of the composites with different TiB2 contents were investigated and compared. The results showed that the B4C–30 vol%TiB2 composite obtained the best comprehensive properties, with a relative density, hardness, bending strength, fracture toughness, and conductivity of 97.9 %, 29.5 GPa, 590 MPa, 6.41 MPa m1/2, and 7.6 × 104 S/m. The compressive stress generated on B4C, crack deflection induced by TiB2, and conductive network formed by TiB2 are of great significance in the context of the properties of the B4C–TiB2 composites. In addition, B4C–TiB2–SiC ternary composites with SiC contents of 0, 10, and 20 vol% were also fabricated by hot pressing. The effect of SiC content on the microstructure and mechanical properties, and the effect of SiC on the antioxidant properties of the composites were investigated. The results showed that the B4C–30 vol%TiB2–10 vol%SiC composite had the best comprehensive properties, with a relative density, hardness, flexural strength, fracture toughness, and residual flexural strength (1600 ℃) of 98.8 %, 29.5 GPa, 621 MPa, 6.80 MPa m1/2, and 465 MPa. The inhibition of the growth of SiC to other grains, removal of oxide impurities, and repair of damage by SiC oxidation products play an important role in the performance of the B4C–TiB2–SiC composites.

Structure and mechanical properties of hot-pressed B4C-NdB6 composites

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Microstructure and mechanical properties of B4C matrix composites prepared via hot-pressing sintering with Pr6O11 as additive

High-performance B4C-YB4 composites fabricated with Y2O3 additive via hot-pressing sintering

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

High-performance B4C matrix composites fabricated from the B4C–Si–CeO2 system via reactive hot pressing

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Enhanced Mechanical Properties of Nanocrystalline B4C–SiC Composites by In-Situ High Pressure Reactive Sintering

Microstructure and mechanical property of B4C–SiC–CrB2 composites fabricated via reactive hot pressing

The Effect of B4C on the Microstructure and Thermo-Mechanical Properties of HfB2-based Ceramics

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites

Microstructure and properties of the C/W2B5 composites fabricated by reaction hot-pressing

Investigation on the preparation and machinability of the B4C/BN nanocomposites by hot-pressing process

High hardness and high fracture toughness B4C-diamond ceramics obtained by high-pressure sintering

Effect of NbC Content on Microstructure and Mechanical Properties of W-NbC Composites

Hard and tough ultrafine-grained B4C-cBN composites prepared by high-pressure sintering

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Microstructure and properties of hot pressed TiB2 and SiC reinforced B4C–based composites

Microstructure and mechanical properties of hot pressed ZrC-SiC-ZrB 2 composites

The effect of B and Ti–Al intermetallics additions on the microstructure and mechanical properties of hot-pressed B4C