Abstract:LuAG:Ce (Lu3Al5O12:Ce) is one of the most important color converters in white lighting industry. Especially, LuAG:Ce film attracts more attention due to the outstanding advantages, such as the efficient heat dissipation, the saving of rare earth, and so on. Here, LuAG:Ce film on sapphire was successfully prepared by the ultrasonic spray pyrolysis process. The phase, microstructure and photoluminescence of LuAG:Ce films were investigated. LuAG:Ce films had a thickness of around 5 μm, which were well crystallized at 1000 °C in air atmosphere to form the typical garnet structure. Under the protection of CO atmosphere, increasing the annealing temperature greatly enhanced the photoluminescence performance. After annealing at 1500 °C for 5 h in CO atmosphere, 3.0 mol.% Ce3+ doped LuAG:Ce film exhibited the highest emission and excitation intensity. The emission intensity of 3.0 mol.% Ce3+ doped LuAG:Ce film annealed at 1500 °C in CO atmosphere increased up to five times, when compared with the best LuAG:Ce film annealed at 1000 °C in air atmosphere. The effects of Ce3+ doping concentration on the photoluminescence were also examined. As the Ce3+ doping concentration increased from 0.2 mol.% to 7.0 mol.%, the color of LuAG:Ce films changed from yellowish green to greenish yellow. When coupling the 3.0 mol.% Ce3+ doped LuAG:Ce film with a 0.5 W 450 nm blue laser, the formed device successfully emitted white light.

Scintillation Properties and Effect of Thermal Annealing in Lu3Al5O12:Ce and Lu3Al5O12:Pr Ceramics

Ce3+, Pr3+ Co-Doped Lu3Al5O12 Single Crystals and Ceramics: A Comparative Study

Stoichiometric modulation and scintillation property characterization of Ce,Ca:LuAG ceramics

Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure, luminescence, and scintillation properties

Warm-white Persistent Luminescence of Lu3Al2Ga3O12:Pr3+ Phosphor

Characterization of Ce,Ca:LuAG ceramic scintillators fabricated from co-precipitated powders

Fast Ce,Ca:LuAG scintillation ceramics for HEP: Fabrication, characterization and computation

Fabrication, Structure and Luminescence Properties of Ce:Lu3Al5O12 Polycrystalline Films

Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Dense Ce3+ doped Lu3A15O12 ceramic scintillators with low sintering adds: Doping content effect, luminescence characterization and proton irradiation hardness

Synthesis and Luminescent Properties of Pr-Doped Lu3al5o12 Translucent Ceramic

The temperature effect of Lu2SiO5:Ce3+ luminescence

Scintillation properties of transparent Lu‐α‐SiAlON:Ce3+ ceramics

Effect of Sc Substitution for Al on the Optical Properties of Transparent Ce : Ysag Ceramics

Ultrasonic Spray Pyrolysis Synthesis and Photoluminescence of LuAG:Ce Thin Films

Concentration and temperature dependence behaviors of photoluminescence and scintillation properties of Lu2O3:Pr single crystals

Structural and Scintillation Properties of Ce3+:Gd3Al3Ga2O12 Translucent Ceramics Prepared by One-Step Sintering

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

On fast LuAG:Ce scintillation ceramics with Ca 2+ co‐dopants

Influence of calcium doping concentration on the performance of Ce,Ca:LuAG scintillation ceramics

Luminescence investigation of Lu2MgAl4SiO12:Ce3+ and Ca2+ substituted Lu2MgAl4SiO12:Ce3+ phosphors