Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Zhou Ding,Shi Ying,Fan Ling-Cong,Lin De-Bao,Sun Ze-Qing,Xu Jia-Yue

DOI: https://doi.org/10.15541/jim20160223

IF: 1.292

2016-01-01

Journal of Inorganic Materials

Abstract:Cerium and Praseodymium co-doped Lu3Al5O12 nanocrystalline powders were synthesized by reverse titration, using ammonium hydroxide (NH4OH) and ammonium hydrogen carbonate (NH4HCO3) mixed precipitator. The optical properties of 0.25at%Pr: LuAG ceramics doped with 0, 0.1at%, 0.2at% and 0.3at% Ce3+ ions were measured. The Ce, Pr: LuAG powders showed a weak agglomeration with a primary particle size of about 60 nm after calcining at 1200 degrees C for 2 h. Ce, Pr co-doped LuAG transparent ceramics were obtained after green compacts were cold isostatic pressed and sintered in flowing H-2 atmosphere at 1800 degrees C for 6 h. The in-line transmittance of the double face polished Ce, Pr co-doped LuAG ceramic at 800 nm wavelength was 82%. The X-ray excited emission spectrum showed that the emission intensity at 550 nm wavelength was enhanced in Ce, Pr co-doped LuAG transparent ceramics by energy transfer from 5d-4f of Pr3+ ions to Ce3+ ions, and the emission intensity reached maximum value when the dopant contents were 0.2at%Ce and 0.25at%Pr.