Abstract:This work is dedicated to investigating the structural, luminescence and photocurrent characteristics of LuAG:Ce single crystalline films grown using the Liquid Phase Epitaxy method on both LuAG and YAG substrates. The primary objective is to analyze the influence of different growth modes, namely homoepitaxial and quasi-homoepitaxial, on the structural and luminescent properties of Ce3+ ions in these films under ambient and high-pressure conditions. Based on the results of X-rays diffraction measurements, we can conclude that both epitaxial structures are fully relaxed. However, a slight deformation of the garnet lattices is observed, manifesting the inequality of the in-plane and out-of-plane lattice constants of substrates and films. The difference in the energy gap values between positions of 4f-5d1,2 Ce3+ absorption bands (6-12 meV) and the positions of Ce3+ emission band (6 meV) was observed for both LuAG:Ce films and caused by the small differences in local perturbations of garnet hosts for epitaxial structures, grown in homoepitaxial and quasi-homoepitaxial modes. The Ce3+ emission intensity in both LuAG:Ce films decrease with temperature in the 10-300 K range. The decay time of the Ce3+ luminescence in LuAG:Ce homoepitaxially-grown film demonstrates a weak temperature dependence in the mentioned range. However, in LuAG:Ce quasi-homoepitaxially-grown film, the decay time of the Ce3+ emission shows notable temperature dependences in the 10-300 K range, probably due to the formation of Ce4+-Pb2+ pair centers. The non-monotonical redshift of the Ce3+ emission band and the increase of the Ce3+ decay time are observed in both LuAG:Ce films under increasing external pressure from ambient to 19 GPa due to the compression and distortion of the crystal lattice. The redshift changes of the Ce3+ emission band on pressure are significantly more complicated for LuAG:Ce quasi-homoepitaxially-grown film than their homoepitaxially-grown counterpart. The outcomes of this study contribute to the fundamental understanding of epitaxial growth processes and their impact on the luminescence characteristics of rare-earth-doped materials in single crystalline film form.

Fabrication, Structure and Luminescence Properties of Ce:Lu3Al5O12 Polycrystalline Films

Ultrasonic Spray Pyrolysis Synthesis and Photoluminescence of LuAG:Ce Thin Films

Ce3+, Pr3+ Co-Doped Lu3Al5O12 Single Crystals and Ceramics: A Comparative Study

Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure, luminescence, and scintillation properties

Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Stoichiometric modulation and scintillation property characterization of Ce,Ca:LuAG ceramics

Scintillation Properties and Effect of Thermal Annealing in Lu3Al5O12:Ce and Lu3Al5O12:Pr Ceramics

Synthesis, Structure and Photoluminescence Properties of Ca2LuHf2(AlO4)3:Ce3+, a Novel Garnet-Based Cyan Light-Emitting Phosphor

Fast Ce,Ca:LuAG scintillation ceramics for HEP: Fabrication, characterization and computation

Optical and structural properties of the Fe 3+ -doped Lu 3 Al 5 O 12 :Ce 3+ garnet phosphor

Luminescence investigation of Lu2MgAl4SiO12:Ce3+ and Ca2+ substituted Lu2MgAl4SiO12:Ce3+ phosphors

Structural, Luminescent Properties and Chemical State Analysis of YAG:Ce Nanoparticle-Based Films

Characterization of Ce,Ca:LuAG ceramic scintillators fabricated from co-precipitated powders

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

Controlled Synthesis and Application of α-Al2O3 for Lu3Al5O12: Ce3+ Green Spherical Phosphors

A comparative analysis of structural and luminescent properties of homoepitaxially and quasi-homoepitaxially grown LuAG:Ce single crystalline films under ambient and high pressure

The Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing CeF <sub>3</sub> :Dy <sup>3+</sup> Nanocrystals

Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing Ceof: Dy3+ Nanocrystals

Dense Ce3+ doped Lu3A15O12 ceramic scintillators with low sintering adds: Doping content effect, luminescence characterization and proton irradiation hardness

Preparation of Ce-Doped Gd3(Al, Ga)5O12 Nanopowders via Microwave-Assisted Homogenization Precipitation for Transparent Ceramic Scintillators

Influence of gallium content on Ga3+ position and photo- and thermally stimulated luminescence in Ce3+ - doped multicomponent (Y,Lu,)3GaxAl5-xO12 garnets