Abstract:The powder material Gd3Ga3Al2O12:Ce (GGAG doped with Cerium) has garnered significant attention in radiation detection due to its high light yield and rapid decay time. Despite its potential, the synthesis of high-quality and reproducible GGAG:Ce scintillating powder remains a considerable challenge. In this study, we present a solvothermal approach with an annealing temperature of 1300 °C for producing cerium-doped GGAG powder with varying concentrations (4, 2, and 0.5 mol%). The structural and luminescent characteristics were meticulously examined using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), photoluminescence (PL), radioluminescence (RL) spectroscopy, and X-ray photoelectron spectroscopy (XPS). XRD analysis confirmed the single-cubic phase garnet structure of the synthesized powder. By comparing the intermediate solvothermal products synthesized at different sintering temperatures (900 °C for 3 hours and 1300 °C for 1 and 3 hours), a direct correlation between solvothermal conditions and the structure/property relationships of the product was established. FESEM images revealed an ellipsoidal to irregular morphology of the as-synthesized GGAG:Ce microparticles, ranging from 0.1 to 0.3 μm, regardless of the Ce concentration. PL spectra demonstrated a strong emission peak at approximately 550 nm, characteristic of Ce3+ ions. RL data confirmed the peak luminescence at around 550 nm, with an almost twofold increase in intensity as the concentration of Ce3+ increased from 0.5 mol% to 4 mol%. XPS data disclosed the Ce3+/Ce4+ ratio in solvothermally synthesized GGAG:Ce, wherein Ce loading of 4 mol% demonstrated the increase in Ce3+ concentration to 95%, whereas the concentration of Ce4+ decreased to 5%. Notably, the highest luminescence efficiency was achieved with GGAG:Ce at a 4 mol% concentration. Thus, the solvothermal method employed in GGAG:Ce synthesis presents a straightforward approach, yielding rapid results with precise control over particle morphology and size.

Characterization of Ce,Ca:LuAG ceramic scintillators fabricated from co-precipitated powders

Fast Ce,Ca:LuAG scintillation ceramics for HEP: Fabrication, characterization and computation

Stoichiometric modulation and scintillation property characterization of Ce,Ca:LuAG ceramics

On fast LuAG:Ce scintillation ceramics with Ca 2+ co‐dopants

Influence of calcium doping concentration on the performance of Ce,Ca:LuAG scintillation ceramics

Dense Ce3+ doped Lu3A15O12 ceramic scintillators with low sintering adds: Doping content effect, luminescence characterization and proton irradiation hardness

Ce3+ doped Lu3Al5O12 ceramics prepared by spark plasma sintering technology using micrometre powders: Microstructure, luminescence, and scintillation properties

Ce3+, Pr3+ Co-Doped Lu3Al5O12 Single Crystals and Ceramics: A Comparative Study

Preparation of Ce-Doped Gd3(Al, Ga)5O12 Nanopowders via Microwave-Assisted Homogenization Precipitation for Transparent Ceramic Scintillators

Scintillation Properties and Effect of Thermal Annealing in Lu3Al5O12:Ce and Lu3Al5O12:Pr Ceramics

Fabrication and Optical Properties of Ce, Pr Co-doped LuAG Transparent Ceramics

Fabrication, Structure and Luminescence Properties of Ce:Lu3Al5O12 Polycrystalline Films

Ultrasonic Spray Pyrolysis Synthesis and Photoluminescence of LuAG:Ce Thin Films

Synthesis and Luminescent Properties of Pr-Doped Lu3al5o12 Translucent Ceramic

Structural and Scintillation Properties of Ce3+:Gd3Al3Ga2O12 Translucent Ceramics Prepared by One-Step Sintering

Microstructure evolution in two-step-sintering process toward transparent Ce:(Y,Gd)3(Ga,Al)5O12 scintillation ceramics

Hydrothermal synthesis of Ce:Lu_2SiO_5 scintillator powders

The Effects of Cation Concentration in the Salt Solution on the Cerium Doped Gadolinium Gallium Aluminum Oxide Nanopowders Prepared by a Co-precipitation Method

The Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing CeF 3 :Dy 3+ Nanocrystals

Scintillation properties of transparent Lu‐α‐SiAlON:Ce3+ ceramics

Synthesis of Cerium-doped Gadolinium Gallium Aluminum Garnet (GGAG:Ce) Scintillating Powder via Solvothermal Method