Abstract:<p>The laser direct deposition, one kind of additive manufacturing technologies, was used to produce W‒Cu composite material. To explain the formation of the deposited microstructure, the process of laser-powder interaction and particle transport phenomena during laser direct deposition were investigated through experiment and simulation works. The parameters of the coaxial powder flow (the distribution and the velocity of flying particles) and the particle motion on the melt pool were demonstrated with high-speed imaging. By using these parameters, a laser-powder flow interaction model was established to calculate the laser intensity attenuated by the powder flow and the temperatures of W and Cu particles. Based on the calculated results, a three-phase fluid dynamics model was constructed to simulate the transport phenomena of W and Cu particles on the substrate surface during laser deposition. The calculated results indicate that the temperatures of W and Cu particles were mainly in the solid state but with huge difference in temperature while arriving at the deposition area. The captured images show that these solid particles can be deposited until the substrate surface was slightly melted. The simulation results suggest that the heat of W particles is conducted to Cu particles rapidly after being deposited on the substrate surface. Coupled with the laser irradiation, Cu particles are melted and form a melt pool. Subsequently, a fallen W particle can float on the melt pool since the inertial force of the falling W particle and the surface tension between Cu and W are roughly balanced. In comparison, if a Cu particle falls on a floating W particle, the Cu particle will be melted and then flow into the melt pool in 300 μs. The combination of high-speed imaging and our simulation explained the deposited microstructure, i.e., the distribution of W particles in the deposition layer.</p>

Effects of Powder-Mixing Homogeneity and W-Powder Morphology on Forming Quality in Laser Direct Forming of W-Cu Composites

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Compaction Behavior and Densification Mechanisms of CuW Composite Powders

Characterization of laser-powder interaction and particle transport phenomena during laser direct deposition of W‒Cu composite

Preparation and Properties of W-15Cu Composite by Electroless Plating and Powder Metallurgy

W–Cu Composite with High W Content Prepared by Grading Rounded W Powder with Narrow Particle Size Distribution

Formation Mechanism of W-coated Cu Composite Powders and the Metal Injection Molding Using Polyoxymethylene-Based Binders

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Effects of Simplified Pretreatment Process on the Morphology of W–Cu Composite Powder Prepared by Electroless Plating and Its Sintering Characterization

Effects of Cu Addition on the Microstructures and Properties of WC-12Co Cemented Carbides Additively Manufactured by Laser Powder-Bed Fusion

Laser Powder Bed Fusion of Pure Tungsten: Effects of Process Parameters on Morphology, Densification, Microstructure

Laser shock dynamic compaction of aluminum–copper (Al–Cu) composite metal powder

The effects of ultrasonic vibration on mechanical properties of tungsten particle-reinforced copper-matrix composites

Study of a New Method to Fabricate W–Cu Composites

Study on forming process and performance of nano-La 2 O 3 reinforced tungsten-based composites by selective laser melting

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Effects of Bonding Treatment and Ball Milling on W-20 wt.% Cu Composite Powder for Injection Molding

The Surface Morphologies and Internal Pores Evolution of a CuSn10 Alloy Fabricated by Laser Powder Bed Fusion

Microstructural studies of W–10wt.% Cu composites prepared by using ultrafine composite powder

Fabrication of W–Cu/La2O3 Composite Powder with a Novel Pretreatment Prepared by Electroless Plating and Its Sintering Characterization

Influence of Laser Texturing on Interfacial Bonding Strength of W/Cu Joint by Spark Plasma Sintering