Abstract:Corrosion defects in steel pipes can lead to pipeline failure, and such failures can have severe impacts; thus, developing appropriate corrosion mitigation schemes to prevent them can be beneficial. To this end, the influences of variables such as the depth, length, and group spacing of corrosion defects on the failure of X80 steel pipes containing group corrosion defects were analysed in this study. Abaqus, a simulation software, was used for non-linear finite element analyses, and 52 groups corresponding to corrosions under different geometric factors were prepared. Furthermore, a pipeline failure pressure prediction model was established using 138 sets of simulations to determine the maximum von Mises stresses of pipelines subjected to internal pressures under different working conditions. Actual blast test data and error comparisons with various existing evaluation standards were conducted to verify the accuracy of the proposed model. The results revealed that an increase in the internal pressure and the changes in the depth, length, and group spacing of group corrosion defects impact the maximum von Mises stress in the pipe. Among the group corrosion defects considered, the depth of the deepest defect was found to be the most critical factor in determining the form of damage and the failure pressure of pipes containing corrosion defects. The length of corrosion defects and the axial spacing between groups of defects were found to be the secondary factors that affect the failure pressure. In an actual pipeline, group corrosion defects are expected to cause a reduction in the wall thickness and, thus, pose a threat to safety, an issue that warrants substantial attention. The results of this work can serve as a reference for assessing the failure of X80 steel pipelines containing group corrosion defects.

Limit Load Capacity of Pipes with Long Longitudinal Corrosion

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Study on the effect of corrosion defects on VIV behavior of marine pipe using a new defective pipe element

Bending Capacity of Corroded Pipeline Subjected to Internal Pressure and Axial Loadings

Analysis on Ultimate Bearing Capacity of Deepwater Submarine Pipe

On Collapse Failure Analysis Of Subsea Corroded Sandwich Pipelines Under External Pressure

Effect of the Y/T on the Burst Pressure for Corroded Pipelines with High Strength

Failure pressure analysis of corroded moderate-to-high strength pipelines

Analytical prediction of failure pressure for pipeline with long corrosion defect

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Mechanical model and probability analysis of buried pipelines failure under uniform corrosion

Effect of Steel Properties on Buckling Pressure of Corroded Pipelines

Theoretical analysis of the collapse behaviour of subsea pipelines with corrosion defects under external pressure

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

Failure Pressure Analysis of the Pipe with Inner Corrosion Defects by FEM

Bending failure of the corroded pipeline subjected to initial internal pressure and axial compressive force

On the effect of long corrosion defect and axial tension on the burst pressure of subsea pipelines

On the Collapse of Thick-Walled Pipes with Corrosion Defects under External Pressure

Evaluating Fitness-for-Service of Corroded Metal Pipelines: Structural Reliability Bases

Buckling response of subsea pipeline with irregular corrosion defect under external pressure